Microstructure and electrical properties of Nd2O3 doped (Bi0.5Na0.5)0.94 Ba0.06TiO3 lead-free piezoelectric ceramics

Changrong Zhou,Liyuan Chai,Xinyu Liu

2010-01-01

Abstract:A new lead-free piezoelectric ceramics of Nd2O3 doped (Bi0.5Na0.5)0.94 Ba0.06TiO3 was prepared by a conventional solid state reaction method. The effect of Nd2O3 doping on microstructure and piezoelectric properties was investigated. X-ray diffraction patterns indicate that neodymium ions diffuse into the lattice of (Bi0.5Na0.5)0.94 Ba0.06TiO3 to form a solid solution with perovskite-type structure. The grain size and morphology vary insignificantly with trace Nd2O3 addition. There are two dielectric abnormal peaks in εr-T curves, and the low abnormal peak shifts to low temperature and εm decreases and the diffuse phase transition characteristics becomes more evident with increasing content of Nd2O3. The optimum piezoelectric properties of kp=0.35 are obtained at d33=173 pC/N, x=0.5% and x=0.3%, respectively.