Abstract:A carbon-coated mesoporous LiFe0.2Mn0.8PO4 solid solution with an olivine structure has been synthesized. Capacities of 140 mAh g(-1) at 1/20C and 80 mAh g(-1) at 2C were achieved at room temperature. A two-phase and a single-phase solid solution mechanism were found for the reactions of Mn2+/Mn3+ and Fe2+/Fe3+, respectively, based on the galvanostatic intermittent titration technique results. The overpotential value of the Mn2+/Mn3+ redox couple was as low as that of the Fe2+/Fe3+ couple. The kinetic property of the Mn2+/Mn3+ redox couple in this material was improved by forming a solid solution and a mesoporous structure.