Abstract:The control of the morphology of nanoparticles is a hot issue all over the world.Organic-inorganic materials can be tailor made with an infinite number of architectures and in diverse forms conveniently.A new type of organic inorganic hybrid material was reported to be synthesized by emulsion polymerization by using the monomers which contained alkoxysilane groups.However,polymerization and morphology could hardly be controled during the emulsion process, because the alkoxysilane group was easy to be subjected to hydrolysis and condensation by sol gel process which decreased the stability of the latex.In the present work, organic inorganic hybrid core shell nanoparticles were synthesized by seeded emulsion polymerization.Through morphology design, polystyrene, as seeded cores, was synthesized firstly, then 3 trimethoxysilyl propyl methacrylate (MPS) was added to form MPS styrene copolymer shell on the surface of polystyrene core. Owing to the hydrolysis condensation of organic alkoxysilane groups in MPS,the organic inorganic hybrid shell was formed through sol gel process.The core shell structure was interpreted by thermodynamical representation and characterized by transmission electron microscopy (TEM).The nonionic surfactant used would decrease the stability of the latex.In acidic condition the latex turned into gel just after the addition of MPS,while,in basic condition the particle number decreased obviously, and the latex kept almost stable in neutral condition.The higher the MPS concentration in the emulsion was,the less stability the latex had.Adding MPS continuously could keep the latex more stable and the particle size could be controlled by this method.Then, the core of this kind of hybrid nanoparticles could be dissolved to yield hollow nanocapsules, with the proportion of the void volume 40 1%.

Capillary Force Induced Formation Of Monodisperse Polystyrene/Silica Organic-Inorganic Hybrid Hollow Spheres

Preparation of monodisperse polystyrene particles and assembly of spherical colloidal crystals

Encapsulation of microgels with polystyrene (PS): A novel method for the preparation of hollow PS particles

Preparation Of Silica-Coated Polystyrene Hybrid Spherical Colloids

Capillary-force-induced Formation of Luminescent Polystyrene/(rare-Earth-doped Nanoparticle) Hybrid Hollow Spheres.

Facile Fabrication and Self‐assembly of Polystyrene–silica Asymmetric Colloid Spheres

Facile approach for the fabrication of monodisperse hollow silica spheres

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

A Novel and Facile Preparation Method of Hollow Silica Spheres Containing Small SiO2 Cores

Formation Mechanism of Monodispersed Polysilsesquioxane Spheres in One-Step Sol-Gel Method

Synthesis of organic-inorganic hybrid core-shell nanoparticles and particle size control

A Method for the Fabrication of Monodisperse Hollow Silica Spheres

Synthesis of Monodisperse Polystyrene@Vinyl-SiO2 Core–Shell Particles and Hollow SiO2 Spheres

A Novel Method for the Fabrication of Monodisperse Hollow Silica Spheres

The Synthesis and Assembly Mechanism of Micro/Nano-Sized Polystyrene Spheres and Their Application in Subwavelength Structures

A Simple and Low-Cost Method for the Preparation of Monodisperse Hollow Silica Spheres

Novel and feasible method for synthesis of monodispersed hollow silicon dioxide submicrospheres

PREPARATION AND CHARACTERIZATION OF PS/SiO2 NANOCOMPOSITE MICROSPHERES

Facile preparation method of SiO2/PS/TiO2 multilayer core-shell hybrid microspheres.

Silica-Coated Core-Shell Structured Polystyrene Nanospheres and Their Size-Dependent Mechanical Properties.

One-step Synthesis of Highly Monodisperse Hybrid Silica Spheres in Aqueous Solution.