Abstract:Indium hydroxide (In(OH)(3)) nanorods and Sn-doped indium oxyhydroxide (InOOH) nanoparticles were synthesized through the hydrothermal method in an aqueous solution. Sodium hydroxide (NaOH) was introduced to adjust the pH value, and sodium acetate (CH3COONa) was employed as the inducer to accelerate the growth along the preferential orientation. Cubic In(OH)(3) was synthesized at pH values ranging from 4.0 to 8.0. In(OH)(3) nuclei grows in the direction {100} into nanorods observed from lattice fringes with an interplanar spacing of about 0.403 nm. The SAED pattern of In(OH)(3) nanorods indicates the rodlike nanocrystal is a single crystal which matches well with the characteristic peaks of cubic In(OH)(3) XRD patterns. The FTIR spectrum signifies the absorption of CH3COO- onto the surface of In(OH)(3) nanorods, which accelerate the growth along the direction {100}. Due to the inhibition effect of OH-, In(OH)(3) particles with a smaller aspect ratio and In2O3 particles with a smaller crystal size were synthesized with the increase of pH values. At a high hydrothermal temperature, cubic In(OH)(3) transformed into orthorhombic InOOH owing to the dopant of Sn with a size smaller than In3+ and r(Sn4+)/r(O2-) = 0.58. The lattice fringes and SAED patterns of InOOH and hexagonal In2O3 nanoparticles were determined. It was also observed that the average size increased from 27 to 46 nm when Sn doping content increased from 2% to 10%. The sensors based on the Sn-doped In2O3 nanoparticles showed a fast (6-7 s) and high response (R-a/R-g = 8.9) to 100 ppm acetone at an operating temperature of 280 degrees C. This work provides a preliminary investigation into the effect of sodium acetate and Sn on the growth of In(OH)(3) nuclei.

Single-Crystalline Semiconductor In(Oh)(3) Nanocubes with Bifunctions: Superhydrophobicity and Photocatalytic Activity

Photocatalytic Activities of Hydrothermally Synthesized In(OH)3 and In2O3 Nanocubes

Nanocrystalline InOOH: Control synthesis and photocatalytic performance in aqueous phase

Synthesis And Photocatalytic Activity Of Single-Crystalline Hollow Rh-In2o3 Nanocrystals

Shape-controlled Synthesis and Photocatalytic Activity of in 2 O 3 Nanostructures Derived from Coordination Polymer Precursors

Indium Hydroxides, Oxyhydroxides, And Oxides Nanocrystals Series

InOOH Hollow Spheres Synthesized by a Simple Hydrothermal Reaction.

In2O3 cubes: synthesis, characterization and photocatalytic properties

A Facile in Situ Fabrication and Visible-Light-Response Photocatalytic Properties of Porous Carbon Sphere/Inooh Nanocomposites

NaNbO3 Nanostructures: Facile Synthesis, Characterization, and Their Photocatalytic Properties

Fabrication of In(OH)3–In2S3–Cu2O Nanofiber for Highly Efficient Photocatalytic Hydrogen Evolution under Blue Light LED Excitation

Fabrication of N-Doped Carbon Quantum Dots/BiOI Nanocomposite and Its Efficient Photocatalytic Activity Under Visible-Light Irradiation

Preparation of In(OH)(3) and In2O3 Nanorods Through a Novel Hydrothermal Method and the Effect of Sn Dopant on Crystal Structures

Tunable Synthesis of Various Hierarchical Structures of In(Oh)(3) and In2o3 Assembled by Nanocubes

C,N-Codoped InOOH microspheres: one-pot synthesis, growth mechanism and visible light photocatalysis

A Facile Hydrothermal Approach for the Deposition of CaIn2S4 Hierarchical Nanosheet Films for Photocatalytic Application

The In2 S3 nanosphere prepared with ultrasonic assistant and its photocatalytic performance

Ag2Se Complex Nanostructures with Photocatalytic Activity and Superhydrophobicity

Anion Exchange Synthesis of Hollow Β-In2s3 Nanoparticles: Adsorption and Visible Light Photocatalytic Performances

Synthesis of Se-doped InOOH As Efficient Visible-Light-active Photocatalysts

Photocatalytic Water Splitting with the Cr-Doped Ba2In2O5/In2O3 Composite Oxide Semiconductors