Abstract:Large-scale arrayed ZnO crystals with a series of novel morphologies, including tower-like, flower-like, and tube-like samples, have been successfully fabricated by a simple aqueous solution route. The morphology and orientation of the obtained ZnO crystal arrays can be conveniently tailored by changing the reactants and experimental conditions. For example, the tower-like ZnO crystal arrays were obtained in a reaction solution system including zinc salt, ammonia, ammonium salt, and thiourea, and the orientation of these tower-like crystals could be controlled by the contents of these reactants. Flower-like ZnO arrays were obtained at lower temperatures, and tube-like ZnO arrays were obtained by ultrasonic pretreatment of the reaction system. The growth mechanism of the tower-like and tube-like ZnO crystals was investigated by FESEM. The results show that tower-like crystals grow layer by layer, while tube-like crystals grow from active nanowires. Ultrasonic pretreatment is proved to be effective in promoting the formation of active nuclei, which have important effects on the formation of the tube-like ZnO crystals. In addition, large-scale arrays of these ZnO crystals can be successfully synthesized onto various substrates such as amorphous glass, crystalline quartz, and PET. This implies this chemical method has a wide application in the fabrication of nano-/microscale devices.

Purposed Built Zno/Zn-5(Oh)(8)Ac-2 Center Dot 2h(2)O Architectures By Hydrothermal Synthesis

Purposed Built ZnO/Zn<sub>5</sub>(OH)<sub>8</sub>Ac<sub>2</sub>·2H<sub>2</sub>O Architectures by Hydrothermal Synthesis

Purposed Built ZnO/Zn5(OH)8Ac2·2H2O Architectures by Hydrothermal Synthesis

Microwave-Assisted Rapid Synthesis Of Zno Hexagonal Quasi-Hourglasses

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Morphology Investigation of Hydrothermally Prepared ZnO Micro-Crystals Influenced by Cu2+ Ions

A Facile Method to Fabricate Superhydrophobic ZnO Nanostructure with Petal Effect

Hierarchical Construction of ZnO Architectures Promoted by Heterogeneous Nucleation

A mantle thermometer

Complex and oriented ZnO nanostructures

ZnO Nano-Rectangular Framework-Like Structure from Zinc Hydroxide Acetate Plates

Large-scale fabrication of tower-like, flower-like, and tube-like ZnO arrays by a simple chemical solution route

Controlled Synthesis of 1D ZnO Nanostructures Via Hydrothermal Process

Morphology regulation, structural, and photocatalytic properties of ZnO hierarchical microstructures synthesized by a simple hydrothermal method

Controllable Growth of ZnO Microcrystals by a Capping-Molecule-Assisted Hydrothermal Process

Facile and Controllable Growth of Zno 1d Nanostructure Arrays on Zn Substrate by Hydrothermal Process

Growth of Arrayed Nanorods and Nanowires of ZnO from Aqueous Solutions

Controllable Growth of Zno Nanostructures by Citric Acid Assisted Hydrothermal Process

Controllable Morphology of ZnO Nanostructures Via a Solvothermal Route

Controllable fabrication of various ZnO micro/nanostructures from a wire-like Zn–EG–AC precursor via a facile solution-based route

Formation Mechanism of Hollow Microspheres Consisting of ZnO Nanosheets