Hydrophilic Dual‐responsive Magnetite/pmaa Core/shell Microspheres with High Magnetic Susceptibility and Ph Sensitivity Via Distillation‐precipitation Polymerization
Wanfu Ma,Shuai Xu,Jumei Li,Jia Guo,Yao Lin,Changchun Wang
DOI: https://doi.org/10.1002/pola.24705
2011-01-01
Journal of Polymer Science Part A Polymer Chemistry
Abstract:A facile and effective approach to preparation of dual-responsive magnetic core/shell composite microspheres is reported. The magnetite(Fe3O4)/poly(methacrylic acid) (PMAA) composite microspheres were synthesized through encapsulating c-methacryloxypropyltrimethoxysilane (MPS)-modified magnetite colloid nanocrystal clusters (MCNCs) with crosslinked PMAA shell. First, the 200-nm-sized MCNCs were fabricated through solvothermal reaction, and then the MCNCs were modified with MPS to form active vinyl groups on the surface of MCNCs, and finally, a pH-responsive shell of PMAA was coated onto the surface of MCNCs by distillation-precipitation polymerization. The transmission electron microscopy (TEM) and vibrating sample magnetometer characterization showed that the obtained composite microspheres had welldefined core/shell structure and high saturation magnetization value (35 emu/g). The experimental results indicated that the thickness and degree of crosslinking of PMAA shell could be well-controlled. The pH-induced change in size exhibited by the core/shell microspheres reflected the PMAA shell contained large amount of carboxyl groups. The carboxyl groups and high saturation magnetization make these microspheres have a great potential in biomolecule separation and drug carriers. Moreover, we also demonstrated that other magnetic polymeric microspheres, such as Fe3O4/PAA, Fe3O4/PAM, and Fe3O4/PNIPAM, could be synthesized by this approach. (C) 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 49: 2725-2733, 2011