Abstract:A novel method for preparation of magnetic composite microspheres was developed by emulsifier-free emulsion polymerization controlled by 1, 1-diphenylethylene (DPE) as free radical polymerization control agent. This paper reported the synthesis of clean composite microspheres with high magnetite content and carboxylic surface by this method. The synthetic strategy is a two-step polymerization. First, some amount of acrylic acid (AA), methyl methacrylate (MMA) and DPE reacted for a few minutes in the presence of persulfate potassium (KPS) as initiator. Subsequently, Fe 3O 4/SiO 2 magnetic fluid prepared by surface modification of Fe 3O 4 nanoparticles with ethyl orthosilicate was added, and the mixture was further polymerized for another time period. Then the system was cooled down to room temperature. The reaction stopped and a precursor polymer which possessed amphiphilic nature and DPE-capped chains was obtained. One end of the precursor polymer chain was linked to the surface of magnetic fluid through chemical adsorption. This not only improved the hydrophobicity of magnetic fluid surface, which stabilized inorganic particles in oil monomers, but also immobilized the potential active species on the surface of nanoparticles. Secondly, the system was heated to a desired temperature and styrene (St) was added to the mixture. The DPE-containing precursor polymer was activated and initiated the monomer polymerization on the surface of magnetic nanoparticles. After a desired reaction time, some amount of acrylic acid was introduced to the system and polymerized for additional hours. At last Fe 3O 4/SiO 2/P (AA-MMA-St) magnetic composite microspheres were obtained. The chemical structure of magnetic fluid and composite microspheres were characterized by Fourier transform infrared spectrometer (FTIR), X-ray photoelectron spectra (XPS). The carboxyl content on the surface of composite microspheres was determined by conductometric titration. The thermoanalysis of composite microspheres was conducted by differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA). The morphologies of magnetic fluid and composite microspheres were observed under a transmission electron microscope (TEM). Particle size determination of composite microspheres was conducted on a laser particle analyzer. The magnetic properties of all magnetic particles obtained were evaluated by using a vibrating-sample magnetometer (VSM). The results of FTIR and XPS indicated the hydrolysate of ethyl orthosilicate formed SiO 2 layers on the surface of Fe 3O 4 nanoparticles. The SiO 2 layer made the saturation magnetization of Fe 3O 4/SiO 2 fall by 3.7% in contrast with Fe 3O 4, but it prevented Fe 3O 4 from reacting with - COOH group, and improved the magnetic property of Fe 3O 4/SiO 2/P(AA-MMA-St) by 28% compared with Fe 3O 4/P(AA-MMA-St) obtained at the same experimental conditions. The TEM observation suggested the composite microspheres possessed core-shell structure. The particle size measurements disclosed the average diameter of composite microspheres was 422 nm and the particle size distribution was narrow, which indicated all the monomers polymerization on the surface of magnetic nanoparticles were controlled effectively by DPE. The TGA analysis revealed the content of inorganic particle (Fe 3O 4/SiO 2) was about 40 % in composite microspheres. The magnetic property evaluation indicated the saturation magnetization of Fe 3O 4/P(AA-MMA-St) was 34.850 emu/g. The conductometric titration result demonstrated the content of carboxyl group on composite microspheres surface was 0.176 mmol/g.DSC analysis showed the glass transition temperature of Fe 3O 4/SiO 2/P(AA-MMA- St) increased by 8.9°C compared with the copolymer of P(AA-MMA-St), which confirmed there was interaction between the core of magnetic nanoparticles and the shell of copolymer.

Preparation of pH-responsive Fe3O4/Poly (acrylic acid-stat-methyl methacrylate-block-(2-dimethylamino) ethyl methacrylate) magnetic composite microspheres and its application in controlled release of drug

Preparation of Thermoresponsive Fe3o4/P(Acrylic Acid-Methyl Methacrylate-N-Isopropylacrylamide) Magnetic Composite Microspheres with Controlled Shell Thickness and Its Releasing Property for Phenolphthalein

Fabrication and caffeine release from Fe3O4/P(MAA-co-NVP) magnetic microspheres with controllable core-shell architecture.

Poly(Acrylic Acid)-Modified Fe3o4 Microspheres for Magnetic-Targeted and Ph-Triggered Anticancer Drug Delivery

Synthesis and characterization of Fe3O4/PPy/P(MAA-co-AAm) trilayered composite microspheres with electric, magnetic and pH response characteristics

Preparation of Magnetic Temperature-responsive Composite Microspheres and Their Drug-release Behaviors Under AC Magnetic Field

PREPARATION OF Fe3O4/SiO2/P(AA-MMA-St) MAGNETICCOMPOSITE MICROSPHERES BY CONTROLLED RADICAL POLYMERIZATION

Preparation Of Fe 3O 4/SiO 2/P(AA-MMA-St) magnetic composite microspheres by controlled radical polymerization

A Novel Route to Prepare Fe3O4/P(MAA-co-NVP) Cross-Linked Magnetic Composite Microspheres with Core-Shell Architecture by Surface-Initiated Radical Dispersion Polymerization.

Mesoporous Fe3O4/SiO2/poly(2-carboxyethyl acrylate) composite polymer particles for pH-responsive loading and targeted release of bioactive molecules

Hydrophilic Dual‐responsive Magnetite/pmaa Core/shell Microspheres with High Magnetic Susceptibility and Ph Sensitivity Via Distillation‐precipitation Polymerization

Research on the Drug Release Behaviors and Mechanisms of Fe3 O4 / (Pnipaam-Co-am) Composite Microspheres

Preparation and characterization of magnetic composite microspheres using a free radical polymerization system consisting of DPE

Dual stimuli-responsive Fe 3 O 4 graft poly(acrylic acid)- block -poly(2-methacryloyloxyethyl ferrocenecarboxylate) copolymer micromicelles: surface RAFT synthesis, self-assembly and drug release applications

Synthesis, characterization, and controllable drug release of pH-sensitive hybrid magnetic nanoparticles

Superparamagnetic pH-sensitive multilayer hybrid hollow microspheres for targeted controlled release

Controlled preparation of Fe 3 O 4 /P (St-MA) magnetic composite microspheres by DPE method

Preparation and Characterization of Multiresponsive Polymer Composite Microspheres with Core–shell Structure

Preparation and drug loading behavior of pH-responsive Fe3O4/CMCS/ALS magnetic nanoparticles

A novel magnetic triple-responsive composite semi-IPN hydrogels for targeted and controlled drug delivery

pH-responsive composite microspheres based on magnetic mesoporous silica nanoparticle for drug delivery.