Abstract:The effect of porosity in composite materials has been studied for years due to its deleterious effects on mechanical properties, especially matrix dominated properties. Currently there is an increasing use of composites in infrastructure worldwide, for example bridge components, residential and building structures, marine structures such as piers and docks, and large industrial chemical tanks. Most of these applications use fiberglass composites. Unfortunately, most of the published literature has focused on carbon fiber composites, in which fiber diameter and gas-fiber interactions are different than fiberglass composites. Therefore, the present study was undertaken to revisit the effect of porosity but specifically in fiberglass composites. The goal of this experimental study was to implement and evaluate various methods for creating porosity in fiberglass composites in a controlled manner in terms of obtaining repeatable void content, morphology, and location within the laminate. The various methods included using different amounts of autoclave pressure, adding a small amount of water between prepreg layers, and using dry fabric layers to starve the laminate of resin. Ultrasonic C-scan nondestructive evaluation was used to assess the quality of the cured panels, as well as optical and electron microscopy and void content measurements via resin burn-out. The cured panels were mechanically tested using the short beam shear (SBS) method. The results showed that the water spray method proved to be the best in terms of producing noticeably different levels of porosity, although the panels required drying to remove residual water after cure. The voids from all three techniques were either oval or elongated in-plane between the plies, but they were not uniformly distributed in-plane. The use of C-scan proved to be helpful for characterizing overall uniformity of each panel, although the results could not be used to directly compare void content between panels. The use of SBS testing was successful for evaluating void dominated properties in panels with high void content, although it was not very sensitive to coupons with lower void contents. Several interesting observations are offered in this manuscript of the fracture surface details and their relation to the SBS load deflection curves. Overall, it was found that the failure mechanisms were mixed mode and the voids did not serve as failure initiation sites. However, the voids participated mainly in the horizontal propagation of cracks between layers, presumably making it easier when they were intersected by a crack and reducing SBS strength.

Effect of void on the interlaminar shear fatigue of carbon fiber/epoxy composite laminates

Critical Void Content for Thermoset Composite Laminates

Thickness Variation Effect on Compressive Properties of Ultra-Thick CFRP Laminates

Out-of-plane Tensile Failure Behavior of Fiber Reinforced Composites Due to Lay-Up Temperature Induced Intra-Ply and Inter-Ply Voids

Effect of Manufacturing Defect on Mechanical Performance of Plain Weave Carbon/epoxy Composite Based on 3D Geometrical Reconstruction

Study of the effect of void defects on the mechanical properties of fiber reinforced composites

Theoretical and experimental analysis on void formation in epoxy composite laminates

Effects of various porosities on the damage evolution behavior of carbon fiber/epoxy composites using acoustic emission and micro-CT

Study on Void Formation in Multi-Layer Woven Fabrics

Investigation of various techniques for controlled void formation in fiberglass/epoxy composites

Effect of Resin-Missing Defects on Tensile Behavior of Carbon Fiber/Epoxy Composites

Interaction of Multiple Micro-Defects on the Strength and Failure Mechanism of UD Composites by Computational Micromechanics

Effect of multi‐angle lamination on mechanical properties and damages behavior of carbon fiber reinforced resin matrix composites

Effect Mechanism and Simulation of Voids on Hygrothermal Performances of Composites

Voids in fiber-reinforced polymer composites: A review on their formation, characteristics, and effects on mechanical performance

Effect of Manufacturing Defects on Mechanical Properties and Failure Features of 3D Orthogonal Woven C/C Composites

Research on Void Dynamics during In Situ Consolidation of CF/High-Performance Thermoplastic Composite

Micro‐mesoscopic analysis of 3D void formation and evolution in CFRP composite using high‐resolution x‐ray microtomography

Influences of Fiber Volume Content on the Mechanical Properties of 2D Plain Carbon-Fiber Woven Composite Materials

Low-velocity impact and compression-after-impact behaviors of twill woven carbon fiber/glass fiber hybrid composite laminates with flame retardant epoxy resin

Investigation on the Mechanical Properties of Epoxy Resin with Void Defects Using Digital Image Correlation and Image-Based Finite Element Method