Surface Engineering to Reduce the Interfacial Resistance for Enhanced Photocatalytic Water Oxidation
Junqing Yan,Jing Liu,Yujin Ji,Munkhbayar Batmunkh,Dan Li,Xiaoshuang Liu,Xingzhong Cao,Youyong Li,Shengzhong Liu,Tianyi Ma
DOI: https://doi.org/10.1021/acscatal.0c02063
IF: 12.9
2020-07-10
ACS Catalysis
Abstract:Interfacial resistance of the charge carriers across TiO<sub>2</sub> to cocatalysts is one of the main limiting factors for realizing high photocatalytic efficiency of water oxidation. Herein, an amorphous TiO<sub><i>x</i></sub> layer is introduced on the surface of crystalline TiO<sub>2</sub> catalyst to form the core–shell structure (<sub>2</sub>) via an oxidation corrosion method. Owing to the surface disordered Ti–O layer, the obtained <sub>2</sub> exposes abundant −OH groups for the homogeneous loading of nanosized IrO<sub><i>x</i></sub>, while the charge carrier interfacial migration is substantially enhanced. The as-prepared IrO<sub><i>x</i></sub><sub>2</sub> exhibits photocatalytic water oxidation performance with an O<sub>2</sub> evolution rate of 143.6 μmol/g·h, which is approximately 14 times higher than that of the bare <sub>2</sub>. Moreover, an apparent quantum yield (AQY) of 18.99% is obtained under LED-405 illumination. This work provides a direction for improving the photocatalytic performance and helps to gain a fundamental understanding of the water oxidation steps.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c02063?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c02063</a>.Experimental section; FTIR spectra, XRD, and N 1s XPS spectra of TiO<sub>2</sub>, CN-TiO<sub>2</sub>, and <sub>2</sub> samples; TEM images of TiO<sub>2</sub> precursor, TiO<sub>2</sub>-ref, and CN-TiO<sub>2</sub> samples; positron annihilation results of TiO<sub>2</sub>, TiO<sub>2</sub>-ref, and <sub>2</sub>; Quasi <i>in situ</i> XPS measurement of CN-TiO<sub>2</sub>-based samples; Raman, FTIR, Ti 2p3/2, O 1s XPS curves, ABPE, and I-t results of TiO<sub>2</sub>-ref, <sub>2</sub>, and IrO<sub><i>x</i></sub><sub>2</sub> samples; BET results; TEM images of IrO<sub><i>x</i></sub>-TiO<sub>2</sub>-ref sample; Ir element line mapping results; element mapping of reference IrO<sub><i>x</i></sub>-TiO<sub>2</sub>-ref sample; optical characteristics of the TiO<sub>2</sub>-ref, <sub>2</sub>, and IrO<sub><i>x</i></sub><sub>2</sub>; online GC signals; O<sub>2</sub> generation of the <sub>2</sub> and TiO<sub>2</sub>-ref samples; O<sub>2</sub> generation rates of the IrO<sub><i>x</i></sub><sub>2</sub> with the different IrO<sub><i>x</i></sub> content loading and the AQY plots; photocatalytic water oxidation performance of samples of IrO<sub><i>x</i></sub>-TiO<sub>2</sub>-ref, IrO<sub><i>x</i></sub><sub>2</sub>-1, and IrO<sub><i>x</i></sub> <sub>2</sub>; O<sub>2</sub> generation values of the TiO<sub>2</sub>-ref and <sub>2</sub> samples under LED-405 and 425 illumination; stability test of the IrO<sub><i>x</i></sub><sub>2</sub>; EIS plots (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c02063/suppl_file/cs0c02063_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, physical