Abstract:Hexagonal boron nitride (h-BN) nanoparticles have attracted increasing attention due to their unique structure and properties. However, it is difficult to synthesize h-BN nanoparticles with uniform spherical morphology due to their crystal characteristic. The morphology control by tuning their precursor synthesis is a promising and effective strategy to solve this problem. Especially, the treatment temperature of precursors plays an important role in the morphology and surface area of h-BN nanoparticles. Herein, h-BN nanoparticles with different morphologies were synthesized via regulating the treatment temperature of precursors. The result shows that treatment temperature will affect the microstructure and state of precursor and further influence the morphology of h-BN products. Benefiting from the unique structure, the h-BN obtained using 250 °C precursors shows higher specific surface area (61.1 m2 g-1) than that of 85 °C (36.5 m2 g-1) and 145 °C (27.9 m2 g-1). h-BN products obtained using 250 °C precursors show higher specific surface area than that of 85 °C and 145 °C. The optimal condition for obtaining high-quality spherical h-BN is the pretreatment temperature of 250 °C and sintering temperature of 1300 °C. Importantly, compared with commercial h-BN nanoparticles, the synthesized h-BN nanoparticles show more uniform structure and larger specific surface area, indicating that sintering activity will be greatly improved. Furthermore, the reaction pathway and formation mechanism of h-BN was revealed by DFT calculations. The result shows that the five stationary states and five transition states exist in the reaction pathway, and the energy barrier can be overcome at high temperatures to form a ring h-BN. In view of its simplicity and efficiency, this work is promising for designing and guiding the synthesis of h-BN nanoparticles with uniform morphology.

Preparation of high purity BCN hollow spheres by pyrolyzing a simple polymeric precursor

A Facile Approach to Fabricate Boron Carbonitride Microspheres Via Precursor Pyrolysis

Synthesis of Bn Microspheres with High-Purity Via A Polymer-Chemical Route

Boron Nitride Microspheres via Pyrolysis of Polymerized Precursors

Direct Synthesis of Sp3‐hybridized BCN Compound by High Pressure and Temperature

Bulk Quantity BCN Microspheres Fabricated by Electrospray from Easily Prepared Precursor

Pressure-induced Vapor Synthesis, Formation Mechanism, and Thermal Stability of Well-Dispersed Boron Nitride Spheres

Preparation of novel carborane-containing boron carbide precursor and its derived ceramic hollow microsphere

Synthesis of high quality inorganic fullerene-like BN hollow spheres via a simple chemical route.

Synthesis of high quality inorganic fullerene-like BN hollow spheres via a simple chemical routeElectronic supplementary information (ESI) available: XPS spectrum of as-prepared h-BN. See http://www.rsc.org/suppdata/cc/b3/b308264d/

Hollow BN microspheres constructed by nanoplates: Synthesis, growth mechanism and cathodoluminescence property

Novel Bn Hollow Microspheres With Open Mouths - Facile Synthesis, Growth Mechanism, Resonant Raman Scattering Effect, And Cathodoluminescence Performance

Fabrication and Characterization of Hollow Spherical Boron Nitride Powders

A Novel Polymeric Precursor for Boron Nitride Ceramics: Synthesis, Characterization, and Ceramic Conversion

High Boron Content and Soluble Polyborosilazanes to Amorphous SiBCN Ceramics

A room-temperature approach to boron nitride hollow spheres

Tailoring Structure and Performance of BCZT Ceramics Prepared Via Hydrothermal Method

Preparation of BN Nanoparticle with High Sintering Activity and Its Formation Mechanism

From Highly Purified Boron Nitride to Boron Nitride‐Based Heterostructures: an Inorganic Precursor‐Based Strategy

Controllable preparation of boron nitride microspheres and their epoxy-based thermoconductive composites

A Facile Route to Prepare Boron Nitride Hollow Particles at 450 °C