Abstract:Nanosilica particles well dispersed in ethanol were modified by 3-(trimethoxysilyl) propyl methacrylate (MPS) and then re-dispersed into methyl methacrylate (MMA) and poly(methyl methacrylate) matrix via a media replacement process and an in situ bulk polymerization process, respectively. The MPS modified status of silica particles and its effects on the dispersion of silica particles in different media and polymer matrix were systematically investigated by FTIR, TG, DLS and TEM. It was found MPS oligomer was the main form for MPS coupling on silica particles surface. Excessive MPS dosage not only resulted in the formation of MPS homo-polymeric particles in media phase, but also the MPS oligomer thick layer on silica surface, which would inevitably induce the small-scale aggregation of silica particles. There existed an appropriate MPS coupling amount for excellent silica dispersity, which is mainly related with the apparent coupling density of MPS molecules on silica particles surface. When the apparent coupling density is 1. 3 similar to 5. 6 mu mol . (m(2) . SiO2)(-1), the MPS coupling efficiency is acceptable and the modification of silica particles is sufficient. Only on this state, silica particles can be dispersed in the monomer and polymer matrix at the primary particles size level, even in the case of 20% silica content. The silica/monomer dispersion prepared via the above processes exhibited high silica dispersity, high silica content, high storage stability and high grafting controllability on silica surface. All of them imply that this kind of dispersion is avail to prepare silica/PMMA composite microspheres via in situ heterogeneous polymerization, and these microspheres would possess controllable morphology and controllable graft interface.

Preparation of ZnO/PMMA Inorganic/organic Composite Microspheres Via Soap Less Emulsion Polymerization

The Preparation And Characterization Of Zns/Pmma Nanocomposites

The Preparation and Characterization of PMMA/POSS-OH Hybrid Fiber

Preparation of Porous Pmma Resin by A New Emulsion Polymerization Process and the Mechanism of Particle Formation

Synthesis at the Nanoscale of ZnO into Poly(methyl Methacrylate) and Its Characterization

Particle Features of A Poly(Methyl Methacrylate) Resin Prepared by A New Emulsion Polymerization Process

Preparation Of Monodisperse Silica/Pmma Core/Shell Nanoparticles With Controllable Shell Thickness By Soap-Free Emulsion Polymerization

Synthesis, Drug Absoprtion and Release Properties of Poly(methyl Methacrylate)/ Poly( 2-Hydroxyethyl Methacrylate) Composite Microspheres

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Synthesis and characterization of PMMA/Al2O3 composite particles by in situ emulsion polymerization

Electrostatic Absorption of Initiator Onto Nanometer SiO2 Particles and In-Situ Emulsion Polymerization of Methyl Methacrylate in the Presence of Modified Nanometer SiO2

Preparation and Properties of Transparent Pmma/Zro2 Nanocomposites Using 2-Hydroxyethyl Methacrylate As A Coupling Agent

Preparation of Sio2/Pmma Organic-Inorganic Hybrid Membrane Via Microemulsion Situ Polymerization Technology

Preparation and Characterization of Silica/Pmma Composites with Highly Dispersed Silica Nanoparticles Dispersion of Nanosilica in Mma

Preparation and Morphology of SiO 2 /PMMA Nanohybrids by Microemulsion Polymerization

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

Synthesis and Characterization of Raspberry-Like Pmma/Sio2 Organic-Inoragnic Composite Particles

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Preparation of SiO2/PMMA Composite Particles Via Conventional Emulsion Polymerization

Fabrication of PMMA/ZnO nanocomposite: effect of high nanoparticles loading on the optical and thermal properties

Preparation of Bigger Core-Shell PS/PMMA Composite Particles by Suspension-Emulsion Combined Polymerization