Synthesis and UV-Curing Kinetics of Epoxy Acrylate Modified by Isocyanate

王锋,胡剑青,涂伟萍

DOI: https://doi.org/10.3969/j.issn.1003-9015.2010.02.009

2010-01-01

Abstract:UV curable epoxy acrylate resin modified by isocyanate (IEA) was prepared with epoxy resin, acrylic acid and isocyanate by two-step method. Elemental analysis, FT-IR and 1H-NMR were used to monitor the structure of the resin, it shows that the prepared resin has lower viscosity of 4500 mPa·s/60℃ and better flexibility below 3 mm. The UV curing kinetics of the resin was studied, and the results indicate that the Irgacure 1000, which is a kind of complex photoinitiators composed by photoinitiators Daeocur 1173 and Irgacurre 184 with mass ratio of 1:1, has the best photoinitiating effect because of its wider absorption band and possible synergistic effect of Daeocur 1173 and Irgacurre 184. The photopolymerization rate and the conversion ratio of the double bonds in the resin increase evidently with the increase of the used amount of photoinitiator Irgacure 1000, while when the used amount of Irgacure 1000 is more than 3%, the photopolymerization rate and the conversion ratio of the double bonds turn to be decrease with the further increase of the Irgacure 1000 amount used. It was found that the more the added amount of activating monomer and the lower the functionality of the activating monomer added, the lower the viscosity of the UV cured system. Since the viscosity of the cured system is the main factor affecting its UV curing behavior, adding more amount of activating monomer with lower functionality will favor the UV curing of the resin, which will increase the curing rate and the terminal conversion ratio of the-C=C-double bonds in the resin evidently. Moreover, increasing the light intensity of the UV radiation can benefit the photopolymerization of the resin too.