Synthesis and Characterization of Incompletely Condensed Heptaphenyltrisilanol-POSS

张文红,王嘉骏,薛裕华,冯连芳,戴黎明

DOI: https://doi.org/10.3969/j.issn.1003-9015.2010.01.019

2010-01-01

Abstract:Using the tetrahydrofuran (THF) as solvent and 40% benzyl trimethyl ammonium hydroxide methanol solution as catalyst, the octaphenyl polyhedral oligomeric silsesquioxane ((C6H5)8T8) was synthesized via the hydrolytic condensation of phenyltrichlorosilane. The obtained (C6H5)8T8 was proved to be precise and pure by FT-IR and 29Si-NMR; then with the help of aqueous tetraethyl ammonium hydroxide (TEAOH) and using the THF as solvent, via the corner-opening reaction; the synthesized (C6H5)8T8 was reacted into the incompletely condensed POSS. In order to suppress the by-product reactions, the corner-opening reaction temperature, time and the amount of catalyst used should be well controlled. The structure of the corner-opening reaction product was determined and validated by 1H-NMR, 13C-NMR, FT-IR, elementary analysis and MALDI-TOF MS. The results indicate that the main product of the corner-opening reaction is heptaphenyltrisilanol-POSS, and its initial decomposing temperature analyzed by TGA is 516.1℃ (5%(wt) weight loss), which suggests that the obtained heptaphenyltrisilanol-POSS has good thermal stability. Compared with literature works, the reaction time of this work is much shorter and thus the yield is increased, which would make the POSS be more useful in the syntheses of organic-inorganic hybrid materials.