Electromagnetic Properties of Ferroelectric/Ferromagnetic Composite Materials Base on Low Temperature Cofired Ceramic Technology

Weiwei Ling,Huaiwu Zhang,Yuanxun Li,Yunsong Xie,Ying He,Long Peng,Feiming Bai
DOI: https://doi.org/10.1063/1.3059599
IF: 2.877
2009-01-01
Journal of Applied Physics
Abstract:The Ni–Cu–Zn ferrite(NCZF)/BaTiO3(BT) composite materials with mass ratio of BT/NCZF (x)=10%, 20%, 30%, and 40% were synthesized by usual ceramic technology and sintered at 900°C to adapt to the low temperature cofired ceramic technology. The sintered density of the composite with x=40% is 5.454g∕cm3 which is higher than that of the Ni–Cu–Zn ferrite (5.349g∕cm3). The composites with x=10% and 20% have stable values of ε′ and lower values of tanδ. The ε′ of the composite with x=40% decreased from 256 to 39 when the frequency increased from 1MHzto1GHz. The microstructures of the sintered ceramics were observed and analyzed by scanning electron microscopy. The permeability spectra of the composites with different BT contents had been resolved into contributions of domain wall resonance and spin rotation relaxation. The fitting results of permeability dispersion revealed the relationships among the above two mechanisms and microstructures. The influences of different composition on the electromagnetic properties of the composites were investigated.
What problem does this paper attempt to address?