Curled Poly(Ethylene Glycol Terephthalate)/Poly(Ethylene Propanediol Terephthalate) Nanofibers Produced by Side-By-Side Electrospinning

Binfei Zhang,Congju Li,Min Chang

DOI: https://doi.org/10.1295/polymj.pj2008270

IF: 3.135

2009-01-01

Polymer Journal

Abstract:The electrospinning process is an established method for producing continuous polymer fibers with diameters on the nanometer scale. In the electrospinning process, a polymer solution is charged with a high electrical voltage. A polymer droplet at the tip of a nozzle is attracted by an electrical field, forming a so-called "Taylor cone." At the tip of the cone. when the droplet overcomes restrictions due to surface tension, a polymer jet is ejected. The charged jet then undergoes bending instability, alternatively referred to as "whipping instability,"(1) stretching itself to form very fine filaments. Solution evaporation from the filament results in dry or semi-dry nanofibers. which are deposited randomly on the collector electrode, usually in the form of a non-woven mat. The whole electrospinning process takes place in milliseconds.(2)Micro- and nanoscale helical structures have been of increasing interesting and have potential applications in areas. such as structure or inductive components in microelectromechanical systems devices, drug delivery systems, and advanced optical components. However, in order to generate helical structures at the micro- or nanoscale, synthesis or processing strategies must be employed. In recent studies, microscale polymeric helical structures were obtained by electrostatic spinning.(3)The formation of large ribbons and loops is prevalent in the electrospinning process and can normally be attributed to the structure and motion of the electrified fluid jet.(4) However, uniform helical structures with microscale coil diameter and the evidence for the existence of it side-by-side bicomponent fiber on morphology have not been report. In this work, helically structured nanofibers were fabricated from two kinds of polymer solution, high shrinkage polyethylene terephthalate (HSPET) and polytrimethylene terephthalate (PTT) in trifluoroacetic acid (TFA)/methylene dichloride component solvent, by using side-by-side eletrospinnig system. A new structure of helical fiber with microscale coil diameter was discovered. The results of this study can provide further insight into the curling mechanism of self-crimp fibers in electrospun.