Properties of the Selective Laser Sintered Specimens of Nylon12-Coated Aluminum Powders

YAN Chun-ze,SHI Yu-sheng,YANG Jin-song,XU Lin
IF: 1.8
2009-01-01
Materials Science and Technology
Abstract:It is difficult for the commonly used mechanical mixing method to uniformly disperse the aluminum powders in the nylon12 matrix,and aluminum coagulation is formed.Therefore,nylon12-coated aluminum powders for the application in the selective laser sintering(SLS) were prepared by a solvent-precipitation method.Microcosmic morphologies of the composite powders were observed using SEM.The effects of aluminum contents and average particle sizes of aluminum powders on the properties of SLS parts were studied.Results show that aluminum particles are uniformly coated by nylon12,and there are almost no naked aluminum particles.When the content of aluminum powders is increased from 0 to 50wt% ,the heat deflection temperature,tensile strength,bend strength,bend modulus,and hardness of the SLS specimens are increased by 87 ℃,10.4% ,62.1% ,122.3% and 70.4% respectively;The tensile strength,elongation at break and impact strength of the SLS specimens are all increased with the decreasing average particle size of aluminum powders.
What problem does this paper attempt to address?