Synthesis of Titanium Dioxide from Blast Furnace Slag Containing Titanium

袁铁锤,刘洪贵,陈晓燕
DOI: https://doi.org/10.3969/j.issn.1673-0224.2009.04.009
2009-01-01
Abstract:After melting vanadic-titanomagnetite in blast furnace, most of TiO2 entered into blast furnace slag as waste. In order to cyclically utilize the titanium resources, using the blast furnace slag containing TiO2 49.36% as raw material prepare titanium materials by roasting with alkali, acid leaching and hydrolysis. It has been found from experimental results that roasting temperature influences TiO2 leaching ratio of blast furnace slag strongly. The leaching ratio is very low when roasting temperature is below 1 000 ℃, but it can be reached to 92.2% at 1 300 ℃. The hydrolysis ratio can be reached to 91.5% when the final acidity is appropriate, the average particle size of TiO2 product ranges from 0.2 μm to 0.5 μm, the grade of TiO2 is 98.50%, and the colour is white or light yellow. All those demonstrate TiO2 product can be used as the raw material for producing sponge titanium.
What problem does this paper attempt to address?