Effect of pre-deformation on hydrogen diffusion and hydrogen induced damage in commercially pure titanium
Zhian Song,Qianqian Wang,Qigui Yang,Te Zhu,Xiaotian Yu,Yunmei Shi,Rui Ma,Mingpan Wan,Peng Zhang,Runsheng Yu,Baoyi Wang,Xingzhong Cao
DOI: https://doi.org/10.1016/j.apsusc.2023.159240
IF: 6.7
2023-12-31
Applied Surface Science
Abstract:This work aims to elucidate the interaction between hydrogen atoms and pre-introduced dislocations in commercially pure titanium (CP-Ti). Positron annihilation spectroscopy supplemented by the first-principle calculations was utilized to reveal the effects of dislocation densities on the formation of hydride types and the concentration of hydrogen-induced defects in CP-Ti. Results show that, in the hydrogen-charged sample with 40 % deformation, hydrogen-induced damage gradually decreases when the hydrogen enters the sample at a depth of about 350 nm. This finding suggests that the high-density dislocations present in deformed specimens effectively trap hydrogen atoms and inhibit their diffusion, which ultimately mitigate damage within the samples. γ-TiH and δ-TiH 2 hydrides are observed in the hydrogen-charged sample. The thermal desorption spectroscopy results show that the desorption amount of deuterium decreases from 1.14 × 10 18 D/cm 2 to 5.10 × 10 17 D/cm 2 with an increase in dislocation density because dislocations inhibit the diffusion of deuterium. In samples with higher deformation, the high dislocation density inhibits the formation of δ-TiH 2 hydrides and promotes the formation of γ-TiH hydrides, which significantly reduce the hardening of samples. These results provide insight into the interaction of hydrogen with pre-introduced defects and provide strong theoretical support for the development and improvement of more damage-resistant materials.
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films