Abstract:Cobalt substituted magnetite, CoxFe1−xFe2O4 was synthesized via co-precipitation method for 0.0≤x≤1.0 and annealed in argon from 600 to 800°C to investigate the effect of synthesis parameters e.g. cation substitution and thermal treatment on its saturation magnetization. Particle size variation, crystallinity and cationic distribution between sublattices which resulted from the varying synthesis parameters are expected to alter the saturation magnetization of cobalt ferrite. Both thermal treatment and cation substitution are affecting the value of saturation magnetization. Correlation of microstructural properties with magnetization were analysed using TG-DTA, XRD, FTIR and VSM. Crystallinity, average crystallite size and lattice constant of the as-annealed samples is increasing with annealing temperature. The presence of maghemite and cobalt oxide as secondary phases have caused reduction in the saturation magnetization. Interestingly, increasing cobalt concentration in the samples has dramatically shifted the temperature at which magnetite transformed to maghemite. We have found that x = 0.4 is the optimum cobalt ratio at which all reactants are converted into reaction product with no incomplete reactions that contribute to the formation of impurities. Preferential occupancy of Co2+ ions on the octahedral sites is evident in the FTIR spectra with intensified octahedral band splitting in the non-stoichiometric CoxFe1−xFe2O4 (0.2≤x≤0.8), whereby the structures formed are in metastable state. It is also evident in the FTIR spectra that distinct absorption bands appeared only when the cations in both sites are well ordered. By substituting Co2+ ions, saturation magnetization keeps on increasing until x=0.4, and gradually reduced beyond that. Highest saturation magnetization (78.86 emu/g) was obtained in Co0.4Fe0.6Fe2O4 after annealing at 800°C. In conclusion, heat treatment and substitution of ferrous/ferric ions with cobalt of lower magnetic moment has amplified the super-exchange interaction between octahedral and tetrahedral sites in magnetite spinel structure for greater saturation magnetization....

Magnetic Properties of FexCo1−x/CoyFe1−yFe2O4 Composite under Hydrothermal Condition

Influence of Co/Fe Ratios on the Structures and the Magnetic Properties of FexCo1−x/CoyFe1−yFe2O4

Soft Magnetism and Microwave Magnetic Properties of Fe-Co-Hf Films Deposited by Composition Gradient Sputtering

Hydrothermal Synthesis and Magnetic Properties of Co X Fe 1−x /co Y La Z Fe 3−y−z O 4 Composites

Syntheses And Properties Of The Fe-Co/Fe3o4 Ferrites

Structure And Magnetic Properties Of Co2.73fe0.27o4 Synthesized By The Heat-Decomposition Method

High Magnetic Performance of Cobalt Ferrite and Anomalous Magnetizing Behavior of Cofe2/Oxide Derived from Ferrite

The Synthesis and the Magnetic Properties of Gd3+-doped FexCo1−x/CoyFe3−yO4 Micro-Octahedrons Composites

Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method

Effect of synthesis parameters on cobalt ferrite saturation magnetization

Nanocomposites of iron-cobalt alloy and magnetite: Controllable solvothermal synthesis and their magnetic properties

Synthesis of Fe–Co Alloy and Cobalt–magnetite Composites Doped with Nd 3+ by Using Iron Disproportionation

Hydrothermal-induced Oriented Growth of Fe–Co Alloy and Sm3+-substituted Magnetite Nanowire Composites

Improved magnetic performance at low and high temperatures in non-exchange-coupling CoFe 2 O 4 /CoFe 2 nanocomposites

Enhanced Magnetic Properties of Xsrfe12o19/(1 − X)cofe2o4 Composites

Synthesis and Magnetic Characterization of Novel CoFe2O4–BiFeO3 Nanocomposites

Composition Dependence of the Magnetic Properties of CoFe2O4/CoFe2 Composite Nano-Ceramics

Preparation of Cobalt- based Fine Alloy Powders and Magnetic Properties

Enhancement of magnetic properties in hard/soft CoFe2O4/Fe3O4 nanocomposites

Strong Magnetoelectric Coupling in CoFe2O4–BaTiO3 Composites Prepared by Molten-Salt Synthesis Method

Preparation and Properties of Fe-Co-Ni Alloy/co0.5ni0.5fe2o4 Magnetic Composite Nanofibers