Effect of multi-pass cooling compression and subsequent heat treatment on microstructural and mechanical evolution of TC4 alloys
Zhaoming Yan,Haijun Liu,Xueyan Dai,Luyao Li,Zhimin Zhang,Qiang Wang,Yong Xue
DOI: https://doi.org/10.1016/j.jmrt.2023.01.217
IF: 6.267
2023-02-19
Journal of Materials Research and Technology
Abstract:Three passes of hot compression tests of hot isostatic pressed Ti-6Al-4V alloys are carried out on a Gleeble-1500D thermo-mechanical simulator with a temperature-drop of 950–900-850 °C, constant strain rate of 0.01∼1 s −1 , and the height reduction from 20% to 70%. Then, the subsequent solution and aging treatments are conducted on a heat treatment furnace. The corresponding results of microstructures and mechanical properties show: In the process of multi-pass deformation, dynamic recrystallization with spheroidization of lamellar α phases are the main characteristics affecting flow behaviors. With the increasing strain, lamellar α phases gradually transform from a bimodal distribution to a single peak state perpendicular to the compression direction. The decreasing length and rising thickness of lamellar α phases in the transformation process facilitate the formation of spheroidized α phases. During the heat treatment, the proportion of spheroidized α phases increases, and the spheroidization phenomenon promotes the reduction of lamellar α phases in length and increment in thickness. Lamellar α phases mainly dominate the contribution of microhardness in the hot compression process, and the equiaxed α phases and β transformation structures are combined to influence the mechanical properties of heat-treated Ti-6Al-4V alloys. Notably, β transformation structures contribute primarily at a higher solution temperature.
materials science, multidisciplinary,metallurgy & metallurgical engineering