Abstract:Nanometer β-Ni(OH)2, showed by XRD, was prepared by our supersonic coordination–precipitation method, with an average grain size of about 50nm by TEM. Proton diffusion coefficient of nanometer Ni(OH)2 and spherical Ni(OH)2 were 1.93×10−11, and 5.50×10−13cm2/s, respectively, with combination of chronocoulometry and cyclic voltammetry. Charge–discharge test of simulated batteries at 0.2°C showed that addition of 8mass% of our prepared nanometer Ni(OH)2 in nickel hydroxide electrodes led to increases in cathode discharge specific capacity (CDSC) by nearly 10% and the chargeability of the electrode by about 50mAh/g, and a decrease in polarization. Cycle life test of AA-type MH-Ni batteries discovered that effect of nanometer Ni(OH)2 in increasing CDSC was more apparent for the first 100 cycles and not much difference was found after 350 cycles. XAS demonstrated a higher oxidation state of Ni in fully charged nanometer Ni(OH)2 composite electrode (Nano-E) and a lower one in discharged Nano-E, compared with micrometer Ni(OH)2 spherical electrodes (Micro-E). A larger structure distortion was found in Nano-E, offering more vacancies for proton diffusion. Thus conversion between Ni2+ and Ni3+ was promoted during the charge–discharge process, which was assumed to be one explanation of increasing CDSC with the addition of nanometer Ni(OH)2.

Effects of Nanoscale Conductive Additives on High Temperature and High Power Performance of Nickel Electrodes

Research on the Nanoscale Additives to the Ni(OH)2 Electrodes for High Power Ni/MH Batteries

Effects of Metallic Cobalt Addition on the Performance of Pasted Nickel Electrodes

Effect of Different Species of Cobalt Additive on Performance of Nickel Hydroxide Electrode

Study of the effects of nanometer ?-Ni(OH) in nickel hydroxide electrodes

Effects of Flaky Rare Earth Oxide Additives on the High Temperature Performance of Nickel Electrodes

Effects of Surface Modification on the Electrode Behavior of Ball-Milled La2Mg17 + 200 Wt% Ni Composite in Alkaline Solution

Electrochemical Performance of the Amorphous Nickel Hydroxide Electrode Material Compounded with Carbon Nanotubes

Study on the influence of nanometric oxide on the electrochemical performance of negative electrode in nickel metal hydride batteries

Effects of Heavy Rare Earth Element on High-Temperature Performance of Nickel-Hydroxide Electrodes

Electrochemical Investigation on Nanoscale CoO As Additive to the Positive Electrodes for Ni/MH Rechargeable Batteries

Effect of Additive Elements on the Performance of the Zr1-xTix(NiCoMnV)2.1 Hydrogen Alloy Electrode

Nanostructured hybrid cobalt oxide/copper electrodes of lithium-ion batteries with reversible high-rate capabilities

Effects of Surface Modification of Nickel Hydroxide Powder on the Electrode Performance of Nickel/metal Hydride Batteries

Synthesis of nanoscale CoO particles and their effect on the positive electrodes of nickel–metal hydride batteries

Effect of Co doping on high rate discharge performance of nano-scale Ni(OH)2

Electrochemical studies of the nickel electrode with cobalt modification

High-rate Dischargeability Enhancement of Ni/MH Rechargeable Batteries by Addition of Nanoscale CoO to Positive Electrodes

The influence of calcium compounds on the behaviour of the nickel electrode

Effects of Hydrothermal Modification on the Electrochemical Properties of Nano-scale Nickel Hydroxide

Effect of Nanometer CuO Additive on the Performance of Hydrogen Storage Alloy Electrode