Abstract:In heat-resistant MgGd based alloys, the relationship between the collective effects of precipitate origin and precipitate-free zone (PFZ) development on the creep resistance is still unclear. In this work, a hot-rolled Mg-13wt%Gd binary alloy was treated by solid solution (SS sample) and peak aging (AA sample). After peak aging, static precipitated β′ phases were widely generated and PFZs were directly formed along both sides of the grain boundaries in AA sample. Tensile creep tests were performed at 523 K on both SS and AA samples. During creep testing, dynamic precipitated β′ phases were gradually generated in SS sample while the β′ phases persisted as large scales in AA sample. The dominant creep mechanisms of SS sample were twinning and cross-slip composed by dislocations, since the late occurrence and low density of β′ phases failed in hindering the movement dislocations at the beginning of steady creep stage. On the contrary, the large-scale β′ phases reduced the space for dislocation movement and succeeded in retarding cross-slip, leading to pyramidal slip being the main creep mechanism of AA sample. Besides, PFZs were formed in SS sample (from zero to ~1.1 μm) while they became narrower in AA sample (from ~5 μm to ~1.7 μm). The large decreased ratio of PFZ width, the large scale of static precipitated β′ phases and the resultant pyramidal slip effectively enhanced the creep resistance of AA sample. Accordingly, AA sample behaved a higher creep resistance in comparison to SS sample at 523 K. It is hoped that the roles of precipitate origin and PFZ development in the creep properties can enrich the theories and methods in improving the service performance of MgGd series at medium to high temperatures.

Characterization of dynamic strain ageing in Mg-3.11wt.%Gd alloy

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Serrated Flow and Tensile Properties of a Mg–Gd–Zn Alloy

An examination of strain ageing in a Mg–Y–Zn alloy containing Gd

The effect of high solid solution Mg contents (7–13 wt%) on the dynamic strain aging behavior of Al–Mg alloys

Tensile Creep Behavior and Microstructure Evolution of Mg-11Gd-2Y-0.5Zr Alloy

Understanding solid solution strengthening at elevated temperatures in a creep-resistant Mg–Gd–Ca alloy

Microstructure Evolution and Mechanical Properties of Directionally Solidified Mg-xGd (x=0.8, 1.5, and 2.5) Alloys

Creep Behaviors of a Highly Concentrated Mg-18 Wt%gd Binary Alloy with and Without Artificial Aging

The Elevated-Temperature Mechanical Behavior of Peak-Aged Mg–10Gd–3Y–0.4Zr Alloy

Creep Behavior of Ageing Hardened Mg-10Gd-3Y Alloy

The Serrated Flow Behavior of Mg-Gd(-Mn-Sc) Alloys

Tensile creep behaviors of Mg-10Gd-0.4Zr alloy under the different applied stresses at 260 °C

The Portevin-Le Chatelier Effect and Creep Behaviour in A Mg-Ca-Zn-Zr Alloy

Effect of Initial Temper on the Creep Behavior of a Mg–Gd–Nd–Zr Alloy

Effects of Precipitate Origin and Precipitate-Free Zone Development on the Tensile Creep Behaviors of a Hot-Rolled Mg-13wt%Gd Binary Alloy

Distinguished Roles of Static Aging and Strain Aging in the Microstructure and Creep Resistance of Mg-4Y-3.5Nd Alloy

Microstructure Analysis, Constitutive Relationship, and Processing Map of Novel Pre-Aged Mg-Zn-Gd-Er Alloy with Different Deformation Ranges

Deformation mechanism of fine grained Mg–7Gd–5Y–1.2Nd–0.5Zr alloy under high temperature and high strain rates

High Temperature Creep Behavior and Creep Microstructure Evolution of T6 State Mg–15Gd Alloy

Tensile creep behaviors of Mg-10Gd-0.4Zr alloy in different heat treatment states