Multiscale Study of the Influence of Promoters on Low-Plasticity Clay Stabilized with Cement-Based Composites
Chuanxin Du,Gang Yang,Tingting Zhang,Qing Yang
DOI: https://doi.org/10.1016/j.conbuildmat.2019.04.094
IF: 7.4
2019-01-01
Construction and Building Materials
Abstract:This study presents the results of the utilization of a cement-based composite stabilizer on soil modification. The effects of additives, including NaOH, CaCl2, Na2SiO3, NaOH/CaCl2 and Triethanolamine, on the engineering properties of clay soil were investigated and evaluated. A series of laboratory tests, including unconfined compressive strength, Atterberg limits, pH, conductivity, XRD, and SEM, were performed. An improvement in the unconfined compressive strength and elastic modulus of the soil, depending on the type and content of additives, was observed. It was found that the cement-based stabilizer supplemented with 1.5% NaOH/CaCl2 could produce more CSH and effectively bond soil particles together, resulting in the most favorable engineering properties. This conclusion was also confirmed by the XRD and SEM results, which showed that the porosity of this sample was lower and that it had a much denser structure than those of the other samples. The strength of the composite stabilizer was 20% higher than that of the soil stabilized with cement The stress-strain curves of the samples indicated that the failure behavior was almost brittle, except for the samples with 1.0%, 1.2%, and 1.5% NaOH. The addition of 1.0%, 1.2%, and 1.5% NaOH resulted in strain-hardening behavior, while the other samples presented strain-softening behavior. In addition, the most appropriate replacement rate of silica fume was selected by changing the substitution rate while the total dry weight of the cement-silica fume mixtures remained unchanged. This investigation suggested that the optimum substitution rate of the silica fume was 40%. The stabilization mechanism of a cement-based composite stabilizer was analyzed using XRD and SEM. (C) 2019 Published by Elsevier Ltd.