Abstract:The currently available high-power laser shows promising opportunities for the welding of thick plates in a single pass. However, weld-root defect frequently occurs when a high-power laser is used to join thick plates in a full-penetration mode, which has a significantly adverse effect on the serviceability of the weld joint. The purpose of this work is to understand the defect formation mechanism and reduce these defects through controlling welding parameters. In this study, the characteristics of weld root defects were investigated using a 10 kW fiber laser using a program of experiment and theoretical analysis. The corresponding defect formation mechanisms were discussed based on the bottom molten pool behaviors observed by the high-speed camera. The results showed that there were four types of weld-root appearances as follows with an increase of linear heat input from 300 J/mm to 1000 J/mm: weld-root humping (30 mm/s), sound weld (25 mm/s), weld sagging (20 mm/s) and excessive weld sagging. The remedies for reducing weld-root defects were also presented to obtain sound weld bead by optimizing welding parameters. Weld-root humping was formed due to the quasi-full-penetration keyhole. Weld sagging resulted from the imbalance of the hydrostatic pressure and surface tension in the condition of a through keyhole. It was also found that the sound weld was formed when a through keyhole and a proper molten pool size were obtained. Thus, the state of the keyhole and molten pool geometry were the major factors that affect weld-root defects.

Criterion for Online Evaluation of Penetration Status in Laser-Mig Hybrid Welding and Its Application

Evaluation Criterion and Closed-Loop Control of Penetration Status During Laser-Mig Hybrid Welding

Penetration status of carbon dioxide laser-MIG hybrid butt welding with various parameters

Vision System for Closed-Loop Control of the Penetration in Laser-Mig Hybrid Welding

Penetration Monitoring and Control of CO 2 Laser Welding with Coaxial Visual Sensing System

Coaxial monitoring and penetration control in CO2 laser welding (I) - Penetration status characteristics and coaxial monitoring

Study on the Method of Vision Detection on Penetration Status in Laser-MIG Hybrid Welding

Online Detection Method of Weld Penetration Based on Molten Pool Morphology and Metallic Vapor Radiation for Fiber Laser Welding

Detection of Backside Width of Molten Pool in Laser-MIG Hybrid Welding

Gap Width Detection and Process Control in Laser Welding with Filler Wire

Penetration prediction of narrow-gap laser welding based on coaxial high dynamic range observation and machine learning

Vision sensing system and detection of backside image of molten pool in laser-MIG hybrid welding

Penetration State Recognition during Laser Welding Process Control Based on Two-Stage Temporal Convolutional Networks

Coaxial Monitoring of Penetration in CO2 Laser Welding

Sensing and Control System of Process Quality in Co2 Laser Deep Penetration Welding

In-process Monitoring of Penetration Depth and Contact Width During Laser Lap Welding Using Fused OCT Depth and Coaxial High Speed Image

Investigation of Weld Root Defects in High-Power Full-Penetration Laser Welding of High-Strength Steel

Gap-detecting Sensor and Wire Feed Control in Butt Laser Welding with Filler Wire

Vision Sensing and Feedback Control of Weld Penetration in Helium Arc Welding Process

Measurement of pulsed laser welding penetration based on keyhole dynamics and deep learning approach

On-line Monitoring of Penetration Status Based on Characteristic Analysis of Arc Sound Signal in MAG Welding