Effects of annealing heat treatment on grain boundary orientation differential evolution of TA15 alloy

Yong Liü,Jingchuan Zhu,Yang Wang

2009-01-01

Rare Metal Materials and Engineering

Abstract:The evolutions of grain boundary orientation differential of TA15 alloy after annealing heat treatments at different temperatures were investigated by EBSD and TEM. The results show a few small-angle grain boundaries of TA 15 alloy transformed into large-angle grain boundaries when annealed at 800 degrees C; more grain boundaries with large angle appeared greatly while annealed at 950 degrees C; the average thermal activation energy was 151.4 kJ/mol for the transformation from small-angle grain boundaries to large angle grain boundaries, which is equal to the self-diffusion activation energy of alpha-Ti; it means that the transformation from the small-angle grain boundaries to the large-angle boundaries was controlled by the self-diffusion of titanium atoms. TEM micrographs show sub grain boundaries transformed into dislocation net with hexagonal net at the annealing temperature of 800 degrees C, while lots of equiaxed grains were obtained after annealing treatment at 950 degrees C.