Preparation of a 58S bioglass/chitosan composite porous scaffold

谢林,陈晓峰,周嘉安,赵娜如,张姝江

2009-01-01

Abstract:Background: Chitosan composite with 58S bioglass scaffold was studied on the basis of prior work in this paper. The bioactivity of the scaffold was also studied through in vitro investigation to see whether it meets the request of tissue engineering. Objective: To investigate the bioactivity and the biocompatibility of the 58S/chitosar composite porous scaffolds with mouse bone marrow mesenchymal stem cells (BMSCs). Design, time and setting: The observational study was performed at the Biomaterials Research Institute, College of Materials Science and Engineering, South China University of Technology from March to October 2008. Materials: The porous bioglass 58S scaffold was prepared by immersion of PU foam with sol-gel derived bioglass powders. The composite scaffold was obtained with the further incorporation of chitosan. Methods: Samples were placed in 100 mL of saline at 37 °C, and immersed for 1, 3, 7 and 15 days, separately for use. At the sixth passage, mouse BMSCs were incubated on the composite scaffold in a 12-well culture plate at the density 2 × 10 5/material. Main outcome measures: X-ray Diffraction and Fourier Transform Infrared Spectroscopy was utilized to investigate the crystalline phase of the materials with different mineralizing time. Scanning Electron Microscopy was used to investigate the formation of the mineral on the surface and the growth of mouse BMSCs on the porous scaffold. Results: From X-ray Diffraction pattern the weak diffraction peaks of hydroxyapatite could be seen after 7 days mineralization in simulated body fluid solution. The intensity of the diffraction peaks became stronger after 15 days mineralization. This showed that crystalline hydroxyapatite was formed on the scaffolds. Fourier Transform Infrared Spectroscopy results indicated that the characteristic peaks of hydroxyapatite appeared after 7 days mineralization. Scanning electron microscope observations showed that particular minerals were formed on the scaffold surface after 1 day mineralization. The minerals covered all the surface of scaffolds after 15 days mineralization. Mouse BMSCs grew well on the scaffolds during the 5 days culture, which suggested the high biomineralization and good cell compatibility of the scaffolds. Conclusion: The porous 58S/chitosan composite scaffold was prepared and showed a good biocompatibility with mouse BMSCs.