Abstract:Core-shell structured SiC/SiO2 nanowires (SiC/SiO2 NWs) were synthesized by a simple thermal evaporation method without a catalyst. The influence of the growth temperature and holding time on the microstructure and composition of the nanowires were investigated. The results indicate that within the temperature range of 1150 to 1550 degrees C, the color of SiC/SiO2 nanowires gradually transitions from pure white to off-white with increasing temperature. During this process, the average diameter of SiC/SiO2 increases from 74 nm to 291 nm, while the surface SiO2 layer thickness decreases from 17 nm to 5 nm, with nanowires can reach lengths of hundreds of micrometres. Variations in supersaturation of SiO and CO at different temperatures lead to discrepancies in nanowire diameter and SiO2 shell thickness. At 1350 degrees C, prolonged holding time enhances silicon powder reaction, resulting in increased structural disorder of the obtained SiC/SiO2 nanowires. The nanowire growth follows a vapor-solid (V-S) mechanism. Additionally, the study demonstrates that the photoluminescence (PL) characteristics of the nanowires exhibit a blue shift attributable to their nanoscale dimensions, while variations in emission spectra correlate with stacking faults, SiC diameter, and SiO2 thickness. This work may be provide a theoretical basis for preparing SiC/SiO2 nanowires with different diameters and SiO2 shell thicknesses, which is crucial for advancing the development and application of SiC/SiO2 nanoceramics.

Large-Scale Synthesis And Raman And Photoluminescence Properties Of Single Crystalline Beta-Sic Nanowires Periodically Wrapped By Amorphous Sio2 Nanospheres 2

Synthesis and Raman Scattering of Β-Sic/sio2 Core–shell Nanowires

Large-Scale Synthesis Of Crystalline Beta-Sic Nanowires

Large-scale Synthesis and Photoluminescence Properties of Hexagonal-Shaped SiC Nanowires

Large-scale synthesis and characterization of hexagonal prism-shaped SiC nanowires.

Large-scale Synthesis of Crystalline Β-Sic Nanowires

Catalytic Synthesis and Growth Mechanism of SiC@SiO2 Nanowires and Their Photoluminescence Properties

Synthesis And Characterization Of Sio2 And Sic Micro/Nanostructures

Large-area highly-oriented SiC nanowire arrays: synthesis, Raman, and photoluminescence properties.

Plasma-assisted Self-Catalytic Vapour–liquid–solid Growth of Β-Sic Nanowires

Synthesis, Structure and Photoluminescence of Twinned SiC Nanowires

Synthesis and Growth Mechanism of Various SiO2 Nanostructures from Straight to Helical Morphologies

Fabrication and Photoluminescence of Hierarchical Sic Nanowires

Tuning the morphologies of SiC nanowires via the control of growth temperature, and their photoluminescence properties.

Synthesis and growth mechanism of SiC/SiO2 nanochains heterostructure by catalyst-free chemical vapor deposition

A Novel Approach To Silicon-Nanowire-Assisted Growth Of High-Purity, Single-Crystalline Beta-Si3n4 Nanowires

In-situ Synthesis of SiC/SiO2 Nanowires by Catalyst-Free Thermal Evaporation of Silicon Powder and Their Photoluminescence Properties

Self-Assembled Hierarchical Single-Crystalline Beta-Sic Nanoarchitectures

Synthesis of In-Situ SiC Nanowires by Self-Assembly Nanoparticles on Carbon Fibers and Their Photoluminescence Properties

Simple Catalyst-Free Method to the Synthesis of Β-Sic Nanowires and Their Field Emission Properties

Synthesis of large-scale SiC@SiO2 nanowires with good optical properties by using Si@SiO2 as silicon source