Abstract:In this paper, porous zinc oxide (ZnO) nanosheets were successfully prepared by a simple low-temperature hydrothermal method. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Brunauer–Emmett–Teller (BET) tests showed that the synthesized product was ZnO with porous sheet structure. The diameter of porous nanosheets was about 100 nm and the thickness was about 8 nm. As a photocatalyst, the degradation efficiencies of porous ZnO nanosheets for methyl orange (MO), methylene blue (MB) and Rhodamine B (RhB) were 97.5%, 99% and 96.8%, respectively. In addition, the degradation efficiency of ZnO for mixed dyes (Mo, MB and RhB) was satisfactory, reaching 97.7%. The photocatalytic stability of MB was further tested and remained at 99% after 20 cycles. In the experiment, ZnO/FTO (fluorine-doped tin oxide) composites were prepared by using ZnO as the conductive layer. Titanium dioxide (TiO2) was deposited on the surface of ZnO/FTO by electrodeposition, so as to obtain a TiO2/ZnO/FTO composite. By studying the electrochromic properties of this composite, it was found that the TiO2/ZnO/FTO composite shows a large light modulation range (55% at 1000 nm) and excellent cycle stability (96.6% at 200 cycles). The main reason for the excellent electrochromic properties may be the synergistic effect between the porous structure and the polymetallic oxides. This study is helpful to improve the photocatalytic efficiency and cycling stability of metal oxides, improve the transmittance of thin films and provide a new strategy for the preparation of ZnO composite materials with excellent photocatalytic and electrochromic properties.

Micro-electrode Ag/ZnO/NiO tri-layer film: Preparation and photocatalytic activity

Surface Morphology, Electrochemical and Electrical Performances of ZnO Thin Films Sensitized with Ag Nanoparticles by UV Irradiation

Effect of solution concentration on surface morphology, optical properties and solar light response of ZnO thin films

Construction of heterojunction ZnFe2O4/ZnO/Ag by using ZnO and Ag nanoparticles to modify ZnFe2O4 and its photocatalytic properties under visible light

Silver-Decorated Tio2 Nanorod Array Films with Enhanced Photoelectrochemical and Photocatalytic Properties

A Very Thin Layer of NiO, Ni(OH)2 Nanosheets Arrays with Organic Functional Modification of Polyaniline

Underlayer Exposure Treatment of ZnO:Al-TiO2 Coupled Film and Investigation to Its Photocatalysis

Enhanced Photocurrent and Photocatalytic Properties of Porous ZnO Thin Film by Ag Nanoparticles

Preparation of ZnFe2O4 nanometer films by sol-gel method and study of its photoelectrocatalytic properties

A Facile Self-assembly Synthesis of Hexagonal ZnO Nanosheet Films and Their Photoelectrochemical Properties

STUDY ON THE PHOTOELECTROCATALYTIC PROPERTIES OF ZnFe_2O_4 AND TiO_2 NANOCOMPOSITE FILMS

Introduction of Ag nanoparticles and AZO layer to prepare AZO/Ag/FTO trilayer films with high overall photoelectric properties

STUDY ON THE INFLUENCE FACTORS OF ZnFe_2O_4 FILMS PHOTOELECTROCATALYTIC PROPERTIES

Construction of Ag Nanosphere-Decorated ZnO Composite Films and Ag’s Crucial Role in Boosting Photocatalytic Performance

Transparent conductive and near-infrared reflective Cu-based Al-doped ZnO multilayer films grown by magnetron sputtering at room temperature

Interfacial Engineering of Ultrathin Metal Film Transparent Electrode for Flexible Organic Photovoltaic Cells

THE OPTICAL AND ELECTRICAL PROPERTIES OF ZnO/Ag/ZnO FILMS ON FLEXIBLE SUBSTRATE

The Synthesis of One Ag@ZnO Micro-nano Composite Structure with High Specific Surface Area and Its Application in Photocatalytic Reduction of Carbon Dioxide

Study on the Photocatalytic Properties with Different Ratio Films of ZnO:Fe<sub>2</sub>O<sub>3</sub>

Synthesis of the Porous ZnO Nanosheets and TiO2/ZnO/FTO Composite Films by a Low-Temperature Hydrothermal Method and Their Applications in Photocatalysis and Electrochromism

Superior Photocatalytic Activities of NiO Octahedrons with Loaded AgCl Particles and Charge Separation Between Polar NiO {111} Surfaces