Quantitative Characterization of the Sulfur-corrosion Reaction and its Influencing Mechanism on the Insulation Paper Aging
YAN Jiangyan,LI Qingmin,ZHOU Yong,HAN Shuai,WANG Zhaodong,LI Chengrong,LIAN Hongsong,ZHENG Dongsheng
DOI: https://doi.org/10.13334/j.0258-8013.pcsee.2015.11.032
2015-01-01
Abstract:To study quantitative characterization of the sulfur-corrosion reaction and its influencing mechanism on the insulation paper aging, accelerated aging tests regarding a corrosive oil sample operational for 6 years were carried out, and comparison were made with a new oil sample denoted as 25# oil. According to measurement of the sulfur concentration and the weight of the oil samples, the sulfur element in the oil was found to increase with time, which indicated that sulfur contents were released from paper pyrolysis and spread into the oil with sulfur concentration rise of the oil. With three specific parameters being combined, namely degree of polymerization (DP), sulfur concentration and weight of the oil, a new method to quantitatively characterize sulfur-corrosion was established. Comparative analysis was done with regard to water moisture, acidity and DP of both the inner and outer layer of paper in the corrosive oil sample. It was found that, with limited oxygen content in the sulfur-corrosive oil-paper insulation, in the initial aging period there was less water moisture in the inner layer of paper than in the outer one, but the gap narrowed later on and finally the inner layer exceeded the outer layer. In the period from time zero to 24h, the acidity of the outer layer paper was a little larger than that of the inner layer, however, the acidity of the inner layer paper increased rapidly in the following period from 24h to 72h and well surpassed the outer layer paper acidity. The DP value of the inner layer paper was always larger than that of the outer layer, but both gradually came closer to each other with the aging time increasing.