Anomalous Magnetic Properties Of An Iron Film System Deposited On Fracture Surfaces Of Alpha-Al2o3 Ceramics

Zhiwei Jiao,Miaogen Chen,WeiDi Jiang,Chunmu Feng,Gaoxiang Ye

DOI: https://doi.org/10.1088/1674-1056/17/9/060

2008-01-01

Chinese Physics B

Abstract:An iron film percolation system is fabricated by vapour-phase deposition on fracture surfaces of alpha-Al2O3 ceramics. The zero-field-cooled (ZFC) and field-cooled (FC) magnetization measurement reveals that the magnetic phase of the film samples evolve from a high-temperature ferromagnetic state to a low-temperature spin-glass-like state, which is also demonstrated by the temperature-dependent ac susceptibility of the iron films. The temperature dependence of the exchange bias field H-e of the iron film exhibits a minimum peak around the temperature T=5K, which is independent of the magnitude of the cooling field Hc(f). However, for T > 10K, (1) H-e is always negative when H-cf=2kOe and (2) for H-cf=20kOe (1Oe approximate to 80 A/m), H-e chantes from negative to positive values as T increases. Our experimental results show that the anamalous hysteresis properties mainly result from the oxide surfaces of the films with spin-glass-like phase.