Composition Anisotropy Compensation and Magnetostriction in Pr(Fe1−xCox)1.9 (⩽x⩽0.5) Cubic Laves Alloys

Y. G. Shi,S. L. Tang,L. Zhai,H. B. Huang,R. L. Wang,J. Y. Yu,Y. W. Du
DOI: https://doi.org/10.1063/1.2938705
IF: 4
2008-01-01
Applied Physics Letters
Abstract:Polycrystalline magnetostrictive alloys Pr(Fe1−xCox)1.9 (0⩽x⩽0.5) with cubic Laves phase were synthesized by high-pressure annealing. Measurements of Curie temperature, easy magnetic direction (EMD), and magnetostriction were made on these alloys. The EMD of the alloys rotates continuously from ⟨111⟩ for x=0.0 to ⟨110⟩ for x=0.3 and then shows a tendency to ⟨111⟩ with further increasing x. Two magnetostriction peaks at low fields are observed around x=0.2 and x=0.4 due to the lower anisotropy of these two alloys, which is consistent with the variation of EMD. This work demonstrates that the composition anisotropy compensation can be realized in Pr(Fe1−xCox)1.9 system.