Abstract:Despite significant efforts to develop ultra-high temperature ceramics, the phase stability together with high hardness and oxidation resistance remains to be addressed in ZrB2-SiC based ceramics. ZrB2-20 vol% SiC (ZS20) ceramics with varying amounts of Si3N4 (2.5, 5 and 10 vol%) were processed by multi stage Spark Plasma Sintering (SPS) over a range of temperature (1800–1900 °C) for 3 min under 50 MPa. All the ZS20-Si3N4 composites could be densified to more than 98% theoretical density (ρth) after SPS at 1900 °C. The XRD, SEM-EDS analysis of the ZS20-Si3N4 composites revealed the presence of reaction product phases (ZrO2, BN, ZrN) along with SiC and ZrB2 major phases. Sintering reactions were proposed to explain the existence of such new phases and extinction of Si3N4. Thermo-Calc software was also used to further confirm the formation of these new phases in the ZS20-Si3N4 samples. The hardness of ZS20-Si3N4 composites varied between 25.50 and 30.56 GPa, in particular, ZrB2-20 vol% SiC-5vol% Si3N4 measured with the maximum hardness. In fact, it is the highest ever reported hardness for the ZrB2 composites. Considering oxidation resistance, the weight gain of ZrB2-20 vol%SiC composites decreased (from 13.84 to 9.84 mg/cm2) and oxide layer thickness increased (64–128 μm) after oxidation at 1500 °C for 10 h in air. The cross sectional microstructure of oxidized ZS20-Si3N4 composites consists of thick dense outer layer of SiO2, intermediate (ZrO2-SiO2) layer and unreacted bulk. The formation of dense SiO2 layer and absence of SiC depleted layer from the oxidized samples are signatures of improved oxidation resistance of Si3N4 reinforced ZrB2-20 vol% SiC.

Microstructure of ZrB2-SiC composite fabricated by spark plasma sintering

SPS Sintering Behavior and Microstructure of ZrB2-SiCpl Composite Ceramics

ZrB2–SiC–G Composite Prepared by Spark Plasma Sintering of In‐Situ Synthesized ZrB2–SiC–C Composite Powders

Spark plasma sintering and hot pressing of ZrB2–SiCW ultra-high temperature ceramics

Low temperature sintering of ZrC-SiC composite

Phase stability, hardness and oxidation behaviour of spark plasma sintered ZrB2-SiC-Si3N4 composites

Microstructure Characterization of ZrB2–SiC Composite Fabricated by Spark Plasma Sintering with TaSi2 Additive

Microstructures and mechanical properties of reactive spark plasma-sintered ZrB2–SiC–MoSi2 composites

Preparation and Properties of ZrB2-SiC Porous Ceramics by Spark Plasma Sintering

Processing and Mechanical Properties of Zirconium Diboride‐Based Ceramics Prepared by Spark Plasma Sintering

SPS densification and ablative performance of ZrB2–SiC–ZrC composites derived from the ternary powders by sol-gel

Spark plasma sintering of B4C–ZrB2 and B4C–ZrB2–SiC ceramics

Microstructure and Mechanical Properties of ZrB2-SiC Composites

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Preparation and interfacial bonding of oversize ZrO2 reinforced metal matrix composites prepared by spark plasma sintering

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

Preparation and Characterization of ZrB 2 -Sic Ultra-High Temperature Ceramics by Microwave Sintering

Pressureless Sintering of ZrB2-SiC Ceramics Incorporating Sol-Gel Synthesized Ultra-Fine Ceramic Powders

Densification, microstructure and mechanical properties of ZrB2–SiCw ceramic composites

Effect of temperature on the structure and mechanical properties of SiC–TiB2 composite ceramics by solid-phase spark plasma sintering

In Situ Synthesis Mechanism and Characterization of ZrB2–ZrC–SiC Ultra High-Temperature Ceramics