Abstract:(1) The simultaneously improved ferroelectric, magnetic and multiferroic properties were achieved in SrTiO3‐modified Bi0.88Sm0.12FeO3 ceramics, which can be attributed to the evolution of electronic state and the transformation of domain structure. (2) The ferroelectric domain changes from micro‐domain (x ≤ .1) to nanodomain (x ≥ .15), and the large remanent polarization was obtained at x = .1, where Pr = 49.0 μC/cm2. (3) Best magnetoelectric properties and enhanced magnetic properties were obtained at x = .1, where Mr = 59.74 emu/mol, αME = .47 mV cm–1 Oe–1. In the present study, SrTiO3 was selected to enhance the multiferroic characteristics of Bi0.88Sm0.12FeO3 (BSF) ceramics. With increasing SrTiO3 content, the principal phase of BSF ceramic transitions from rhombohedral R3c to Pna21. Through DSC and dielectric analysis, it was observed that both the Curie temperature and Néel temperature decreased proportionally with the augmentation of SrTiO3 content. When x = .1, the optimal ferroelectric performance is achieved, and the highest remanent polarization value is 55.47 μC/cm2, significantly surpassing that of BSF ceramics. Moreover, the PFM test results showed that as the substitution content increased, the domains in the BSF ceramic gradually transformed from normal ferroelectric domains to polar nanomicro‐domains. Magnetic and magnetoelectric results show that when x = .1, the best magnetic properties are obtained, Mr = 59.7 emu/mol. The magnetoelectric coefficient αME initially increased and then decreased with the increasing SrTiO3 content, reaching its optimum magnetoelectric properties at x = .1, where αME = .47 mV cm–1 Oe–1. In summary, when the substitution amount of SrTiO3 reaches 10%, the ferroelectric, magnetic, and magnetoelectric properties of BSF ceramics are significantly improved.

Enhanced ferromagnetic properties of multiferroic Bi1-xSrxMn0.2Fe0.8O3 synthesized by sol-gel process

Structural, Magnetic, and Dielectric Properties of Sol-Gel-Derived Multiferroic Bi[sub 1−x]sr[sub X]fe[sub 0.8]mn[sub 0.2]o[sub 3] Ceramics

Structure and magnetic characterization of Sr-doped BiFeO3 prepared by sol–gel method

Simultaneously Enhanced Ferroelectric and Magnetic Properties in Fe-substituted Ba4Sm2Fe Ti4-2Nb6+O30 Ceramics

Effects of Sr-substitution on Structure, Dielectric, Ferroelectric and Magnetic Properties of (Srxba1-X)4sm2fe2nb8o30 Ceramics

Magnetic and Electrical Properties of Bi0.8Ca0.2Fe1−xMnxO3 (0≤X≤0.5)

Evolution of structure, magnetism and ferroelectricity in the (1-x)BiFeO3-xBa0.5Sr0.5MnO3(0≤x≤1) solid solutions

The Magnetic Properties of Polycrystalline Bi1−xSrxFeO3 Ceramics

Enhanced Ferromagnetic Properties Of Multiferroic Bicoxfe1-Xo3 Synthesized By Hydrothermal Method

Multiferroic And Magnetoelectric Properties Of Bi(1-X)Baxfe(1-X)Mn(X)O(3) System

Effect of Mn Substitution on Microstructures, Dielectric and Magnetic Properties of BiFeO<sub>3</sub> Ceramics

Multiferroic and magnetoelectric properties of Bi<sub>1−<i>x</i></sub>Ba<sub><i>x</i></sub>Fe<sub>1−<i>x</i></sub>Mn<sub><i>x</i></sub>O<sub>3</sub>system

Effect of Mn Substitution on Microstructures, Dielectric and Magnetic Properties of BiFeO3 Ceramics

Structural, Magnetic and Ferroelectric Properties of Sm and Mn Co-Substituted BiFeO3 Ceramics with Composition Near the Morphotropic Phase Boundary

Simultaneously enhanced ferroelectric and magnetic properties of SrTiO3‐modified Bi0.88Sm0.12FeO3 ceramics

Structural Evolution and Multiferroic Properties in the Vicinity of MPB of Ca2Bi4Ti5-xMnxO18 Solid Solutions

Multiferroic properties and converse magnetoelectric effect in Bi1−xCaxFeO3 ceramics

Enhanced Magnetic and Optical Properties of Pure and (mn, Sr) Doped BiFeO3 Nanocrystals

Influence of substitution of different transition metal elements (Mn, Cr, Co) on the properties of Bi0.88Sm0.12FeO3-based ceramics

Improved Room-Temperature Multiferroicity in Co-doped Aurivillius Sr0.5Bi5.5Fe1.5Ti3.5O18 Ceramics

Ferroelectric and Ferromagnetic Properties of Mn-doped 0.7bifeo3–0.3batio3 Solid Solution