Abstract:Two kinds of adsorbates—L-ascorbic acid and NaOH were used separately to investigate the effects of adsorbate distribution between ethanol bulk phase and the phase of water-rich layer adsorbed by the surface of SiO2 particles on the preparation of silver nanoparticles on SiO2 particles. When the adsorbate L-ascorbic acid was used, L-ascorbic distributes mainly in the ethanol bulk phase and thus the Ag particle generating reaction will take place in the ethanol bulk phase with the generated Ag particle size of about 18 nm. When the adsorbate NaOH was used, NaOH distributes mainly in the phase of water-rich layer adsorbed on the surface of SiO2 particles and thus the Ag particles generate in the water-rich adsorption layer with particle size of only about 5.4 nm. Since the NaOH concentration effects its distribution between the two phases of ethanol bulk phase and water-rich adsorption layer, the further experiments with changing NaOH concentration in the reaction system from 0.0170 to 0.404 g·L-1 were conducted. Results show that when concentration of NaOH in the system was increased from 0.0170 to 0.135 g·L-1, the NaOH concentration in the water-rich adsorption layer increases with the increase of NaOH concentration in the system gradually, which causes the generation of Ag grains gradually centralizes in the adsorption layer with the grain size decreases from 8 nm to 5 nm, and the Ag particles generated cover the SiO2 more uniformly. When NaOH concentration in the system was increased from 0.135 to 0.404 g·L-1, the amount of NaOH in the system is over the maximum NaOH capacity that can be contained in the water-rich adsorption layer and thus the NaOH concentration in ethanol bulk phase will increase to the limit, above which, the Ag generating reaction rate in it will accelerate more quickly than that in the water-rich adsorption layer, which causes the main generation zone of silver nanoparticles moves from water-rich adsorption layer to ethanol bulk phase gradually, and at the same time, the generated Ag grain size will increase from 5 nm to 12 nm.

Effect of Nonionic Surfactant on Seeded Precipitation of Sodium Aluminate Solution

Effect of Polyamidoamine on Surface Tension and Seed Precipitation in Sodium Aluminate Solution

Effect of Interphase Distribution of Reactants in Binary Liquids on Preparation of Silver Nanoparticles on Silica Particles

Effect of nitrate or sulfate on flocculation properties of cationic polymer flocculants

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Influences of Seeds on the Properties of Zeolite NaA Membranes on Alumina Hollow Fibers

[Coagulation Characteristics of Surfactant SDBS Micellar Solution with Aluminum Salt].

A Kind Of Activity Seed Used For The Precipitation Of The Sodium-Aluminate Liquor

Effect of Surfactant on the Physical Properties of Hierarchically Macro–Mesoporous Metal Oxides

Preparation of Near-Spherical α-Al2O3 Particles by Enhanced Precipitation of Gibbsite from Sodium Aluminate Solution Using Highly Dispersed Al2O3 as Seeds

Effects of SO42- on the Heterogeneous Precipitation Coating of Hydrous Alumina on TiO2 Particles in an Aqueous Process

Effects of Methanol on the Seeded Precipitation of Al(OH)3 from Potassium Aluminate Solution

Effect of impurity ions on the primary nucleation of ammonium alum precipitated from aqueous solution

Effect of Surfactants on Synthesis of Tio2 Nano-Particles by Homogeneous Precipitation Method

Effects of Precipitators and Surfactants on the Preparation of Zirconia Nanopowders via Solvothermal Method

Secondary Nucleation Of Aluminium Trihydroxide In Bayer Sodium Aluminate Solution

Effects of Non-Ionic Surfactant Adding to Sodium Aliphatate on the Three Phase Contact Angle

EFFECT OF DIFFERENT SURFACTANTS ON THE DISPERSION OF ZINC OXIDE POWDERS

Preparation and characterisation of seed for simultaneous removal of sulphur and iron from sodium aluminate solution

Adsorption of salicylic acid, 5-sulfosalicylic acid and Tiron at the alumina–water interface

Effect of co-precipitation synthesis parameters on gadolinium aluminate nanoparticles