Abstract:A series of sulfonated copolyimides containing benzimidazole groups (SPIs) were synthesized by random copolymerization of 1,4,5,8-naphthalenetetracarboxylic dianhydride (NTDA), 2-(4-aminophenyl)-5-aminobenzimidazole (APABI), 4,4′-diaminodiphenyl ether-2,2′-disulfonic acid (ODADS) and 9,9-bis(4-aminophenyl)fluorene (BAPF) in m-cresol in the presence of benzoic acid and triethylamine at 180 °C for 20 h. Membranes with good mechanical properties were prepared by solution cast method. Proton exchange treatment resulted in ionic cross-linking and the membranes were further covalently cross-linked by treating them in polyphosphoric acid (PPA) at 180 °C for 6 h. The covalently cross-linked membranes displayed slightly lower ion exchange capacities (IECs) and proton conductivities than the corresponding covalently uncross-linked ones because small part of the sulfonic acid groups had been consumed during the cross-linking process. Fenton’s test (3% H2O2 + 3 ppm FeSO4, 80 °C) revealed that benzimidazole groups played an important role in the radical oxidative stability of the membranes, while the cooperative effect of benzimidazole groups and covalent cross-linking led to much more significant enhancements in the radical oxidative stability of the membranes than each alone. The membrane 4 (ODADS/APABI/BAPF = 2/1/1, by mol), for example, after covalent cross-linking could maintain membrane form within 8 h measurement, which was much longer than that (3 h) before covalent cross-linking under the same conditions. The membrane 5 (ODADS/BAPF = 3/1, by mol) without benzimidazole groups, however, after covalent cross-linking started to break into pieces after 85 min measurement, which was only slightly longer than that (60 min) before cross-linking under the same conditions.

Preparation of Novel Six-Member Sulfonated Polyimide Proton Exchange Membranes

Sulfonated Polyaryletherketone with Pendant Benzimidazole Groups for Proton Exchange Membranes

Synthesis and Properties of Benzimidazole Group-Containing Sulfonated Polyimide Proton Exchange Membranes

Synthesis And Characterization Of Novel Sulfonated Polyimide Membranes

Preparation and Characterization of Novel Sulfonated Polyimide Proton Conductive Membrane

Synthesis and properties of side-chain-type wholly aromatic sulfonated polyimides

Synthesis and Properties of Novel Sulfonated Polyimides from 4,4′-(Biphenyl-4,4′-diyldi(oxo))bis(1,8-naphthalic Anhydride)

Synthesis and properties of highly sulfonated proton conducting polyimides from bis(3-sulfopropoxy)benzidine diamines

Synthesis, Water Stability and Proton Conductivity of Novel Sulfonated Polyimides from 4,4′-Bis(4-aminophenoxy)biphenyl-3,3′-disulfonic Acid

Sulfonated copolyimide membranes derived from a novel diamine monomer with pendant benzimidazole groups for fuel cells

Synthesis and Properties of New Sulfonated Naphthalenic Polyimides As Proton Exchange Membrane for Fuel Cell Applications

Novel Acid–base Polyimides Synthesized from Binaphthalene Dianhydrie and Triphenylamine-Containing Diamine As Proton Exchange Membranes

Preparation of novel naphthalenic sulfonated polyimide proton conductive membrane

Synthesis, proton conductivity and methanol permeability of a novel sulfonated polyimide from 3-(2′,4′-diaminophenoxy)propane sulfonic acid

Sulfonated polyimides: Synthesis, proton conductivity and water stability

Synthesis and properties of highly sulfonated proton conducting polyimides from bis(3-sulfopropoxy)benzidine diaminesElectronic supplementary information (ESI) available: 1H NMR spectra of BSPB diamines and IR spectra of resulting polyimide membranes. See http://www.rsc.org/suppdata/jm/b3/b313276e/

Preparation and Properties of Covalently Cross-Linked Sulfonated Copolyimide Membranes Containing Benzimidazole Groups

PREPARATION AND CHARACTERIZATION OF SOLUBLE SULFONATED POLYBENZIMIDAZOLE FOR PROTON EXCHANGE MEMBRANE MATERIALS

Synthesis, Proton Conductivity and Chemical Stability of Novel Sulfonated Copolyimides-Containing Benzimidazole Groups for Fuel Cell Applications

Novel Preparation Method of Cross-Linked Sulfonated Polyimide Membranes for Fuel Cell Application

Synthesis and Properties of Novel Sulfonated Polyimide Membranes for Direct Methanol Fuel Cell Application