Susceptibility to hydrogen embrittlement and dehydrogenation annealing process of bainite steel used for crossing

Chun-lei ZHENG,Fu-cheng ZHANG,Bo L(U),Tian-sheng WANG,Yang-zeng ZHENG

2008-01-01

Abstract:The dehydrogenation annealing process of bainitic steel used for crossings were carried out, according to the solubility and diffusion of hydrogen in steel. The critical hydrogen concentration and susceptibility to hydrogen embrittlement of bainitic steels were studied by slow strain rate tensile test. The reuslts show that the microstructure of the experimental steel is refined by the process. Plasticity and toughness of the steel are greatly enhanced. The hydrogen content of W-containing steel decreases from 1.2 × 10 -4% to 0.5 × 10 -4% which is lower than the critical hydrogen concentration of 0.7 × 10 -4%. Hydrogen content of Mo-containing steel decreases from 1.6 × 10 -4% to 0.4 × 10 -4% which is lower than critical hydrogen concentration of 0.6 × 10 -4%. Susceptibility to hydrogen embrittlement of W-containing steel is lower than that of Mo-containing steel.