Cooling Precipitation and Strengthening for Different Locations of a Powder Metallurgy Nickel-Base Superalloy Disk

TIAN Gao-feng,JIA Chenge-hang,WEN Ying,LIU Guo-quan,HU Ben-fu

2008-01-01

Abstract:The precipitation behavior of γ′ phase precipitated during cooling at different locations of a new type powder metallurgy(P/M) nickel-base superalloy disk was studied by simulating heat treatment tests on a simulator,interrupted cooling tests were applied to investigate the development of γ′ precipitates and strength of the disk in the process of cooling.The results show that the γ′ precipitates with more complex shape at bore location exhibit larger and wider variation sizes compared with those at rim location.Wider grain boundary at bore location is observed,and ultimate tensile strength of disk bore is lower than that of disk rim.The mean size of secondary γ′ precipitates at bore and rim locations linearly increases with the decrease of interrupt temperature,and the growing rate at bore location is larger.The strength of the alloy is decreases firstly and then increases with decreases of the interrupt temperature,which is believed to associate with the multi-stage nucleation of γ′ precipitates during cooling process.