Microstructure characterization of nickel matrix composite reinforced with tungsten carbide particles and produced by laser cladding
Josef Domitner,Zahra Silvayeh,Ricardo Henrique Buzolin,Sabine Krisam,Klaus Achterhold,Erwin Povoden-Karadeniz,Christof Sommitsch,Peter Mayr
DOI: https://doi.org/10.1002/adem.202200463
IF: 3.6
2022-06-30
Advanced Engineering Materials
Abstract:Wear‐resistant metal matrix composites (MMC) are common engineering materials which have been used for many industrial hardfacing applications. This work provides the detailed characterization of a laser‐clad MMC consisting of hard tungsten carbide particles embedded in a comparatively soft nickel alloy matrix, which has been intended to be used for potential rolling mill applications. Special focus of the investigations was placed on the relationship between the microstructure of the as‐deposited reinforcing particles and their hardness. Therefore, thermally induced dissolution of carbides caused by laser metal deposition (LMD) processing was studied. The methods of investigation include X‐ray diffraction (XRD), X‐ray micro‐computed tomography (μCT), transmission electron microscopy (TEM) with selected area electron diffraction (SAED), as well as scanning electron microscopy (SEM) combined with energy‐dispersive X‐ray spectroscopy (EDS), electron backscatter diffraction (EBSD) and nanoindentation. The as‐received powder blend mainly consisted of fused spherical particles of ditungsten carbides (W2C, W2C1–x) and monotungsten carbides (WC, WC1–x). Dissolution of large particles at the matrix/particle interfaces and fragmentation or even complete dissolution of small particles due to the high process temperature of LMD was observed. Primary W2C/W2C1–x phases were partially dissoluted and layers of secondary WC/NixWyC phases formed at the matrix/particle interfaces. As these surface layers were less hard than the as‐received particles, the local hardness gradually decreased from the inner region of the particles across the surface layer towards the matrix, which is supposed to improve bonding of particles inside the matrix. The hardness was dependent on the grain size and on the crystal structure of the carbides. Even when the crystal structures were identical, particles consisting of fine grains had considerably higher hardness than particles consisting of coarse grains. This article is protected by copyright. All rights reserved.
materials science, multidisciplinary