Abstract:Strong mechanical properties and controllable biodegradability, together with biocompatibility, are the important requirement for the development of medical implant materials. In this study, an ultraviolet (UV) radiation method was developed to achieve controlled degradation for bacterial biopolyester poly (3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) which has a low biodegradation rate that limits its application for many implant applications required quick degradation. When UV radiation was applied directly to PHBHHx powder, significant molecular weight (Mw) losses were observed with the powder, Mw reduction depended on the UV radiation time. At the same time, a broad PHBHHx Mw distribution was the result of inhomogeneous radiation. Interestingly, this inhomogeneous radiation helped maintain the mechanical properties of films made of the UV-radiated powder. In comparison, the PHBHHx films subjected to direct UV radiation became very brittle although their degradation was faster than that of the PHBHHx powders subjected to direct UV radiation. After 15 weeks of degradation in simulated body fluid (SBF), films prepared from 8 and 16h UV-treated PHBHHx powders maintained 92% and 87% of their original weights, respectively, while the untreated PHBHHx films lost only 1% of its weight. Significant increases in growth of fibroblast L929 were observed on films prepared from UV-radiated powders. This improved biocompatibility could be attributed to increasing hydrophilic functional groups generated by increasing polar groups C-O and CO. In general, UV-treated PHBHHx powder had a broad Mw distribution, which contributed to fast degradation due to dissolution of low Mw polymer fragments, and strong mechanical property due to high Mw polymer chains. Combined with its improved biocompatibility, PHBHHx is one more step close to become a biomedical implant material.

In vitro investigation of maleated poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) for its biocompatibility to mouse fibroblast L929 and human microvascular endothelial cells.

Effect of surface treatment on the biocompatibility of microbial polyhydroxyalkanoates.

In vitro study on hemocompatibility and cytocompatibility of poly(3-hydroxybutyrate-co -3-hydroxyhexanoate)

Effect of lipase treatment on the biocompatibility of microbial polyhydroxyalkanoates

Effects of Surface Morphology on the Biocompatibility of Polyhydroxyalkanoates

Application of Microbial Polyesters-Polyhydroxyalkanoates As Tissue Engineering Materials

In Vitro Biocompatibility and Degradation of Terpolyester 3Hb-Co-4hb-co-3hhx, Consisting of 3-Hydroxybutyrate, 4-Hydroxybutyrate and 3-Hydroxyhexanoate.

The Mechanical Properties and in Vitro Biodegradation and Biocompatibility of Uv-Treated Poly(3-Hydroxybutyrate-Co-3-Hydroxyhexanoate)

Effect of Composition of Poly(3-Hydroxybutyrate-Co-3-Hydroxyhexanoate) on Growth of Fibroblast and Osteoblast

Reduced mouse fibroblast cell growth by increased hydrophilicity of microbial polyhydroxyalkanoates via hyaluronan coating.

Effects of surface modification of poly (3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) on physicochemical properties and on interactions with MC3T3-E1 cells.

In Vivo Studies of Poly(3-Hydroxybutyrate-co-3-hydroxyhexanoate) Based Polymers: Biodegradation and Tissue Reactions.

Cellular Compatibility of Blends Consisting of Poly (3-Hydroxybutyrate-co-3-hydroxyhexanoate) and Polyethylene Glycol

Improved Mechanical Property and Biocompatibility of Poly(3-Hydroxybutyrate-co-3-hydroxyhexanoate) for Blood Vessel Tissue Engineering by Blending with Poly(propylene Carbonate)

Biocompatibility studies and characterization of poly(3-hydroxybutyrate-<i>co</i>-3-hydroxyhexanoate)/polycaprolactone blends

Biocompatibility studies and characterization of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate)/polycaprolactone blends.

Studies on Bone Marrow Stromal Cells Affinity of Poly (3-Hydroxybutyrate-co-3-hydroxyhexanoate)

Polyhydroxyalkanoate (PHA) Scaffolds with Good Mechanical Properties and Biocompatibility

Evaluation of PHBHHx and PHBV/PLA Fibers Used As Medical Sutures.

Influence of DL-beta-hydroxybutyric acid on cell proliferation and calcium influx.

Effect of 3-hydroxyhexanoate content in poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) on in vitro growth and differentiation of smooth muscle cells.