Abstract:Strong mechanical properties and controllable biodegradability, together with biocompatibility, are the important requirement for the development of medical implant materials. In this study, an ultraviolet (UV) radiation method was developed to achieve controlled degradation for bacterial biopolyester poly (3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) which has a low biodegradation rate that limits its application for many implant applications required quick degradation. When UV radiation was applied directly to PHBHHx powder, significant molecular weight (Mw) losses were observed with the powder, Mw reduction depended on the UV radiation time. At the same time, a broad PHBHHx Mw distribution was the result of inhomogeneous radiation. Interestingly, this inhomogeneous radiation helped maintain the mechanical properties of films made of the UV-radiated powder. In comparison, the PHBHHx films subjected to direct UV radiation became very brittle although their degradation was faster than that of the PHBHHx powders subjected to direct UV radiation. After 15 weeks of degradation in simulated body fluid (SBF), films prepared from 8 and 16h UV-treated PHBHHx powders maintained 92% and 87% of their original weights, respectively, while the untreated PHBHHx films lost only 1% of its weight. Significant increases in growth of fibroblast L929 were observed on films prepared from UV-radiated powders. This improved biocompatibility could be attributed to increasing hydrophilic functional groups generated by increasing polar groups C-O and CO. In general, UV-treated PHBHHx powder had a broad Mw distribution, which contributed to fast degradation due to dissolution of low Mw polymer fragments, and strong mechanical property due to high Mw polymer chains. Combined with its improved biocompatibility, PHBHHx is one more step close to become a biomedical implant material.

Effect of surface treatment on the biocompatibility of microbial polyhydroxyalkanoates.

Effect of lipase treatment on the biocompatibility of microbial polyhydroxyalkanoates

Effects of Surface Morphology on the Biocompatibility of Polyhydroxyalkanoates

Effect of Composition of Poly(3-Hydroxybutyrate-Co-3-Hydroxyhexanoate) on Growth of Fibroblast and Osteoblast

In vitro investigation of maleated poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) for its biocompatibility to mouse fibroblast L929 and human microvascular endothelial cells.

Effects of surface modification of poly (3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) on physicochemical properties and on interactions with MC3T3-E1 cells.

Reduced mouse fibroblast cell growth by increased hydrophilicity of microbial polyhydroxyalkanoates via hyaluronan coating.

In vitro study on hemocompatibility and cytocompatibility of poly(3-hydroxybutyrate-co -3-hydroxyhexanoate)

Cellular Compatibility of Blends Consisting of Poly (3-Hydroxybutyrate-co-3-hydroxyhexanoate) and Polyethylene Glycol

Application of Microbial Polyesters-Polyhydroxyalkanoates As Tissue Engineering Materials

In Vivo Studies of Poly(3-Hydroxybutyrate-co-3-hydroxyhexanoate) Based Polymers: Biodegradation and Tissue Reactions.

Properties of Poly(3-Hydroxybutyrate-co-3-hydroxyhexanoate) Films Modified with Polyvinylpyrrolidone and Behavior of MC3T3-E1 Osteoblasts Cultured on the Blended Films

Production and functionalization strategies for superior polyhydroxybutyrate blend performance

The cytocompatability of polyhydroxyalkanoates coated with a fusion protein of PHA repressor protein (PhaR) and Lys-Gln-Ala-Gly-Asp-Val (KQAGDV) polypeptide.

Improved Mechanical Property and Biocompatibility of Poly(3-Hydroxybutyrate-co-3-hydroxyhexanoate) for Blood Vessel Tissue Engineering by Blending with Poly(propylene Carbonate)

Biocompatibility of a New Biodegradable Poly Butylene Carbonate Electrospun Film

Improvement of Mechanical Properties of Poly(dl-Lactide) Films by Blending of Poly(3-Hydroxybutyrate-co-3-hydroxyhexanoate)

Evaluation on cytotoxicity of biodegradable material-PHBV in vitro

The Mechanical Properties and in Vitro Biodegradation and Biocompatibility of Uv-Treated Poly(3-Hydroxybutyrate-Co-3-Hydroxyhexanoate)

Biocompatibility studies and characterization of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate)/polycaprolactone blends.

Effect of 1,4-bis(tert-butyl peroxy isopropyl) benzene on the rheological, mechanical, thermal and barrier properties of poly(butylene succinate-co-terephthalate)/poly(lactic acid) blends and blown films