Abstract:The paper presented an experimental study on the effect of the resin reinforced core configuration and core thickness on in-plane compressive responses and failure behaviors of composite sandwich specimens. Two resin reinforced core machining configurations were designed with three core thickness along. In-plane compressive load, displacement, strains on both sides, and failure morphology were closely monitored during the loading process. Meanwhile, the theoretical method also was supplementary to forecast the failures of sandwich structures. It was found that the enhancement of grooved, perforated holes and contour cut (GPC) core was better than double-side grooved and perforated hole (DGP) core to improve the in-plane compressive capacity of sandwich specimens for all thick cores. The core fracture or skin/core debonding failure of sandwich specimens resulted in an instant drop of in-plane compressive load, and the global buckling led to a slower reduction. The failure mode changed from global buckling to skin/core debonding at both sides as the core thickness increased for the Plain core sandwich specimen; switched from global buckling to a combined failure of core fracture and skin/core debonding at both sides, and then to skin/core debonding at both sides for the DGP core sandwich specimen; the skin/core debonding at the shallow side occurred for all GPC core specimens. The slight buckling trace of strains before the peak load probably triggered the skin/core debonding of sandwich specimens. The theoretical method could well forecast failure loads and corresponding failure modes of sandwich specimens with the 15 mm thick core, and reasonably predict failure loads for sandwich specimens with 30 mm and 45 mm thick cores.

Compression Property Analysis of X-cor Sandwich Composites

Three-point bending behaviors of the foam-filled CFRP X-core sandwich panel: Experimental investigation and analytical modelling

Experimental study on the compression-after-impact behavior of foam-core sandwich panels

Analysis of Buckling Failure Modes of Composite Sandwich Panels Filled with Aluminum Foam

Compression Performance and Analytical Model of Hexagonal-Core Sandwich Panels Fabricated by 3D Printed Continuous Carbon Fiber-Reinforced Thermosetting Epoxy Composites

Investigation on the shear behaviors of carbon fiber composite sandwich panels with the X-core

In-plane compressive response of composite sandwich panels with local-tight honeycomb cores

Fabrication and Mechanical Characterization of CFRP X-core Sandwich Panels

Mechanical Properties Test and Failure Analysis of Composite Foam Sandwich Structure in Ramp-Down Zone

Prediction and Experiment on the Compressive Property of the Sandwich Structure with a Chevron Carbon-Fibre-reinforced Composite Folded Core

Fabrication and Flatwise Compression Property of Glass Fiber-Reinforced Polypropylene Corrugated Sandwich Panel

In-plane compressive responses and failure behaviors of composite sandwich plates with resin reinforced foam core

Compressive Strength and Energy Absorption of Sandwich Panels with Aluminum Foam-Filled Corrugated Cores

Compression Response of Sandwich Structure with M-Type CFRP Foldcore

Effect of Core Architecture on Charpy Impact and Compression Properties of Tufted Sandwich Structural Composites

Edgewise compressive test and analysis for lattice web reinforced composite sandwich panels with foam core

Influence of Geometric Parameters on Flatwise Compression Properties of a Novel Lattice Sandwich

Experimental Investigation of 3d Sandwich Structure with Core Reinforced by Composite Columns

Effects of Process Parameters upon Shear Modulus of X-cor Foam Sandwich Structure

Buckling Analysis of Hybrid Fiber‐reinforced Composite Sandwich Panels with Varying Numbers of Polyurethane Cores

Effect of an S-shaped reinforced core on the compression properties of composite honeycomb sandwich panel and tube structures