Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Preparation and Photoluminescence of Single-Crystalline GdVO4:Eu3+ Nanorods by Hydrothermal Conversion of Gd(OH)3 Nanorods

Synthesis and photoluminescence of octahedral GdVO4 microcrystals by hydrothermal conversion of Gd2(CO3) 3·xH2O nanospheres

Facile Hydrothermal Synthesis and Luminescent Properties of Large-Scale GdVO<sub>4</sub>:Eu<sup>3+</sup>Nanowires

Sensitized Deep-Ultraviolet Up-Conversion Emissions of Gd3+ Via Tm3+ and Yb3+ in Hexagonal NaYF4 Nanorods

Sensitized deep-ultraviolet up-conversion emissions of Gd 3+ via Tm 3+ and Yb 3+ in hexagonal NaYF 4 nanorods

Highly Uniform Gd(Oh)(3) And Gd2o3:Eu3+ Nanotubes: Facile Synthesis And Luminescence Properties

Hydrothermal Synthesis and Luminescence Properties of NaGdF4:Eu3+ Crystals

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Morphologies of GdBO3:Eu3+ One-Dimensional Nanomaterials

Rare earth activated nanosized oxide phosphors: synthesis and optical properties

Hydrothermal synthesis and photoluminescence of single-crystalline LaVO4:Eu3+ nanorods/nanosheaves

Preparation and luminescence properties of Gd2 (MoO4 )3 :Eu3+ red phosphors with high colour purity

Hydrothermal Synthesis and Luminescent Properties of CexGd1−xF3:Ln3+nanocrystals

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Fluorescent-magnetic Nanocrystals: Synthesis and Property of YP(x)V(1-x)O4:Eu@GdPO4 Core/shell Structure.

Surfactant-assisted Synthesis and Luminescent Properties of Gd2O3:Eu3+ Core–shell Microspheres

Preparation and Luminescent Properties of 1d Lu2o2s:Eu3+ Nanorods

Preparation and photoluminescence of yttrium hydroxide and yttrium oxide doped with europium nanowires

Study of Vacuum Ultraviolet and Ultraviolet Excitation Spectra of GdVO4∶Eu 3+

Study on VUV and UV Excitation Spectrum of GdVO 4 ∶eu 3+

Systhesis, phase transformation and photoluminescence properties of Eu:La 1-xGd xVO 4 nanofibers by electrospinning method