Effect of Li Content on the Surface Film Formed on the Binary Mg–Li Alloys in NaCl Solution
Chuanqiang Li,Dahui Liang,Yejia Lin,Yong Dong,Binqing Shi,Changjian Yan,Zhengrong Zhang
DOI: https://doi.org/10.1007/s12540-023-01495-7
IF: 3.451
2023-07-31
Metals and Materials International
Abstract:The surface film formed on the Mg–Li alloys with different Li content in 0.1 M NaCl solution were investigated via electrochemical testing, morphologies observation and chemical composition analysis in this work. The results revealed that the surface film of Mg–14Li alloy (L14: body centred cubic (BCC)) possessed higher electrical resistivity and remained a higher tolerating over-potential (0.1 V vs. open circuit potential) than those of Mg–4Li (L4: hexagonal closed-packed (HCP)) and Mg–7.5Li (L7: HCP+BCC), resulting in a better corrosion performance. After 24 h immersion in NaCl solution, the whole surface film of L14 remained undamaged and displayed weave-like and dense characteristic, while both L4 and L7 present a severely damaged film. The cross-sectional details illustrated typical two layers of surface film formed on L14 with the outer layer of ~ 1.5 μm and inner layer of ~ 2.5 μm in thickness, whilst only one layer of film with less than 2.5 μm in thickness was observed on L4 and L7. At last, combining analysis of X-ray diffraction, energy dispersive X-ray spectrometry, X-ray photoelectron spectroscopy and transmission electron microscope confirmed the composition of outer layer of surface film on the L14 contains much more Mg(OH)2 and Li-containing compounds, and the porous Mg(OH)2 film can be sealed by the Li-containing compounds, which is very different the single Mg(OH)2 film on the traditional magnesium and L4/L7 alloys. As a result, the best protective function of the surface film on the L14 alloy contribute to its high corrosion resistance.Graphical Abstract
materials science, multidisciplinary,metallurgy & metallurgical engineering