AC corrosion of steel pipeline under cathodic protection: A state‐of‐the‐art review
Emadoddin Majdabadi Farahani,Yuhan Su,Xiao Chen,Hao Wang,Tyler R. Laughorn,Frank Onesto,Qixin Zhou,Qindan Huang
DOI: https://doi.org/10.1002/maco.202313955
2023-09-28
Materials and Corrosion
Abstract:A state‐of‐the‐art review on alternating current (AC) corrosion of cathodically protected pipeline steel is presented. The review covers key research areas, such as influencing factors of AC corrosion, existing criteria for AC protection, corrosion risk evaluation based on the probability of failure, numerical simulations of AC corrosion, and strategies for mitigating AC corrosion. By the advancement of the oil, electricity, and transportation industries, an increasing number of oil and gas pipelines were buried alongside high‐voltage alternating current (AC) transmission lines and electrified railways. This resulted in a growing issue of AC interference in buried pipelines. Previous studies have shown that the presence of AC interference can result in severe corrosion damage to metallic structures, even when cathodic protection (CP) is available. This paper provides a state‐of‐the‐art review on AC corrosion of cathodically protected pipeline steel. Specifically, attention is paid to research areas including influencing factors in AC corrosion for pipelines under CP, existing AC protection criteria, corrosion risk assessment based on probability of failure, numerical simulation in AC corrosion, and mitigation of AC corrosion. Each area of research is reviewed in detail and the corresponding technical gaps and future research opportunities are identified and discussed.
materials science, multidisciplinary,metallurgy & metallurgical engineering