INFLUENCES OF PHOSPHORUS PENTOXIDE ON SINTERING BEHAVIORS OF GLASS-CERAMICS FROM PHOSPHORUS SLAG

曹建尉,梁开明,李要辉

DOI: https://doi.org/10.3321/j.issn:0454-5648.2008.10.023

2008-01-01

Abstract:Glass-ceramics were prepared from phosphorus slag as the main raw material by sintering method. The factors influencing the sintering behavior were investigated by orthogonal test and X-ray diffraction. The results show that the dominant factor is sinter-ing temperature, the second is P2O5 content, the third is the particle size, and the last is the holding time. P2O5 had a significant effect on the sintering behavior when the other three influential factors were invariable. When the P2O5 content (mass fraction, the same below) was less than 1.8%, β-CaSiO3 was the main crystalline phase at below 1 000 ℃ and the surface of the glass-ceramics was not smooth. When the P2O5 content was more than 3.6%, the required sintering temperature was increased to 1 100 ℃ ; meanwhile, the required holding time was dramatically prolonged. In this case, Na2Ca2Si3O9 became mainly crystalline and the surface of the glass-ceramics was not smooth. As a result, the preferential P2O5 content was in the range of 1.8%–3.6%, sintering temperature was 1 000–1 050 ℃, sintering time was 60 min, and glass-ceramics with a smooth and flat surface could be obtained.