Abstract:Si3N4 saw-tooth nanoribbons (SNSNs) have been synthesized via a novel approach involving a by-product pyrolysis-nitridation process during carbon foam manufacturing at 1450 degrees C. The SNSNs formed are ribbon shaped, 80-750 nm wide, 70-80 nm thick and several micrometres in length. The process simply involved thermal pyrolysis of a powdered mixture containing carbon foam precursors and silicon powder under flowing high-purity nitrogen. Pyrolysis gases rich in silicon, silicon oxide and active nitrogen vapours promoted the subsequent synthesis of the SNSNs over the outer surface of the carbon foams via a vapour-solid mechanism. The crystal structure, morphology, chemical composition, growth mechanism and photoluminescence (PL) properties have been studied. The infrared adsorption of SNSNs exhibited two absorption bands with all the peaks related to the Si-N bonds of the alpha-Si3N4 crystalline structure. X-ray photoelectron spectroscopy measurements further confirmed the chemical composition, with minor impurities such as oxygen and carbon. A single nanoribbon has the same width-to-thickness ratio, suggesting a stable morphology resulting from the reduction of the overall surface energy. Intense PL was observed centred at 2.03, 2.48, 2.62, and 3.01 eV, which resulted from the recombination between the intrinsic conduction band edges and silicon dangling bonds with deep-level or trap-level states.

Catalyst and Temperature Dependent Growth of Silicon Nitride Micro/Nanoribbons

Ultrafast growth of single-crystalline Si nanowires

Controlled Al-doped single-crystalline silicon nitride nanowires synthesized via pyrolysis of polymer precursors.

Synthesis And Growth Mechanism Of Silicon Nitride Nanostructures

A Simple Approach to Controllably Grow Network-Like Branched Single-Crystalline Si3n4 Nanostructures

In-Situ Synthesis and Growth Mechanism of Silicon Nitride Nanowires on Carbon Fiber Fabrics

Synthesis of N-Type SiC Nanowires with Tailored Doping Levels

Growth and Mechanism of Network‐Like Branched Si3N4 Nanostructures

Morphology Control of Si-Based Nanostructures by Catalyst-Assisted Pyrolysis of Preceramic Precursors

Morphology-Controlled Synthesis of SiC Nanowires by Catalyst-Assisted Pyrolysis of Polymeric Precursor

Role of Catalyst in Controlling the Growth and Morphology of One-Dimensional Sic Nanostructures

Tunable Morphology and Photoluminescence of Uniform -Si3n4 Microribbons

Controlled Growth of One-dimensional 3C–SiC nanostructures with stable morphology

Controllable growth of high-density tapered N-doped SiC nanowires arrays

Systematic Investigation of the Formation of 1D Alpha-Si(3)n(4) Nanostructures by Using a Thermal-Decomposition/nitridation Process.

Synthesis and Characterisation of Self-Assembled SiC Nanowires and Nanoribbons by Using Sol–gel Carbothermal Reduction

Ferrocene‐Catalyzed Growth of Single‐Crystalline 6h‐sic Nanoribbons

Co-Catalyzed Nitridation Of Silicon And In-Situ Growth Of Alpha-Si3n4 Nanorods

Study on polymeric precursor pyrolysis synthesis and growth mechanism of Si3N4 nanobelts

By-product processing of Si3N4 saw-tooth nanoribbons during carbon foam processing using pyrolysis–nitridation reactions

Adjusting the Morphology and Properties of SiC Nanowires by Catalyst Control