Abstract:<p>Dynamic failures (e.g., crater, crack and spall) can be observed in concrete structures when suffered from possible blast and impact loadings. Understanding the physical mechanisms behind these failures needs a sound material model that thoroughly considers the damage mechanisms of concrete material, especially under the high confinement situation existed near the projectile and explosion. Modelling the damage mechanisms is a challenging problem that is not fully resolved in the commonly-used concrete material models. In this study, three kinds of damage mechanisms of concrete material, i.e., the hydrostatic damage due to pore collapse, shear damage due to shear-induced microcracking and tensile damage due to tensile microcracking are identified and physically modelled respectively using corresponding damage indexes. The interaction of the three damage is also considered by introducing two stress-dependent factors. The damage model is implemented into the Kong-Fang material model recently proposed, in which improvements on the strength surfaces, strain-rate enhancement and erosion criterion are accompanied made based on a few years use of this model. Numerical triaxial compression test and hydrostatic compression to unconfined compression test are conducted using a single element to validate the proposed hydrostatic damage model and the shear damage model. And the competition mechanism between hydrostatic damage and shear damage during the triaxial compression test is discussed. Then the modified Kong-Fang model is used to numerically simulate the reinforced concrete slabs subjected to a contact explosion load and projectile impact load, in which the physical mechanisms of the experimentally observed crater, crack, tunnel and spall failures are revealed.</p>

Static and Dynamic Meso-Failure-mechanism of Concrete under Confined Compression

Stochastic Fracture of Concrete Composites: A Mesoscale Methodology

Mesoscopic numerical test of crushing process of concrete under uniaxial compression

Micromechanics Model for Static and Dynamic Strength of Concrete under Confinement

Meso-mechanism of Effects of Free Water on Mechanical Properties of Concrete under Confined Compression

New concrete cracking model established based on fracture mechanics and damage theory

Experimental study on fracture properties of self-compacting concrete

3D Mesoscale Fracture Analysis of Concrete under Complex Loading

Micro-mechanism of Static and Dynamic Strengths for Saturated Concrete

Dynamic Constitutive Equations for Concrete Based on Meso-Cracks and a Static Constitutive Model

Damage Based Constitutive Model for Predicting the Performance Degradation of Concrete

A Microscopic Approach to Rate Effect on Compressive Strength of Concrete

Dynamic fracture of concrete in compression: 3D finite element analysis at meso- and macro-scale

Theoretical characterization of mesoscopic dynamic fracture behaviors of concrete based on an extended self-consistent finite stress model (XSFSM)

Mesoscopic Numerical Simulation of Fracture Process and Failure Mechanism of Concrete Based on Convex Aggregate Model

A microscopic approach to rate effect on concrete strength under combine load

Modelling damage mechanisms of concrete under high confinement pressure

Mesoscale Modelling of Concretes Subjected to Triaxial Loadings: Mechanical Properties and Fracture Behaviour

Determination of Intergranular and Transgranular Failure of Mesoscale Model Concrete under Mode-I Fracture

3D meso‐scale numerical model and dynamic mechanical behavior of reinforced concrete

Study of dynamic behavior of concrete under splitting tensile tests based on mesomechanics