Abstract:The giant magnetoresistance (GMR) and structure was investigated for electrodeposited Co/Cu multilayers prepared by a conventional galvanostatic/potentiostatic pulse combination from a pure sulfate electrolyte with various layer thicknesses, total multilayer thickness and Cu deposition potential. X-ray diffraction (XRD) measurements revealed superlattice satellite reflections for many of the multilayers having sufficiently large thickness (at least 2 nm) of both constituent layers. The bilayer repeats derived from the positions of the visible superlattice reflections were typically 10-20% higher than the nominal <a class="link-external link-http" href="http://values.The" rel="external noopener nofollow">this http URL</a> observed GMR was found to be dominated by the multilayer-like ferromagnetic (FM) contribution even for multilayers without visible superlattice satellites. There was always also a modest superparamagnetic (SPM) contribution to the GMR and this term was the largest for multilayers with very thin (0.5 nm) magnetic layers containg apparently a small amount of magnetically decoupled SPM regions. No oscillatory GMR behavior with spacer thickness was observed at any magnetic layer thickness. The saturation of the coercivity as measured by the peak position of the MR(H) curves indicated a complete decoupling of magnetic layers for large spacer thicknesses. The GMR increased with total multilayer thickness which could be ascribed to an increasing SPM contribution to the GMR due to an increasing surface roughness, also indicated by the increasing coercivity. For multilayers with Cu layers deposited at more and more positive potentials, the GMRFM term increased and the GMRSPM term decreased. At the same time, a corresponding reduction of surface roughness measured with atomic force microscopy indicated an improvement of the multilayer structural quality which was, however, not accompanied by an increase of the superlattice reflection intensities.

Relation Between Giant Magnetoresistance And Interlayer Exchange Coupling In The Magnetic Multilayers

THEORY OF GIANT MAGNETORESISTANCE IN NONMULTILAYER MAGNETIC SYSTEMS

Quantum Theory for Interfacial Roughness and Angle Dependence of Giant Magnetoresistance in Magnetic Multilayers

Exchange Coupling in Sputtered Giant Magnetoresistance NiFe/Cu/CoFe/Cu Multilayers

Giant magneto-impedance effect in Ni80Fe20 composited multilayers

The Interlayer Exchange Coupling in Magnetic Multilayers: the Effect of the Thickness of the Ferromagnetic Layer

Giant Magnetoresistance in Fe/In Multilayers and Its Anomalous Temperature Dependence

Observation Of Giant Magnetoresistance In Fe/Mo Multilayers

Perpendicular transport and magnetization processes in magnetic multilayers with strongly and weakly coupled magnetic layers

Giant magnetoresistance in a three-dimensional lattice of dipolar interacting magnetic nanoparticles

Study on the Interfacial Characterization of the Co-5/Cu-3/Co-5 Trilayer and Co-3/Cu/Co/Cu-3/Co/Cu/Co-3 Multilayer

Interfacial Roughness and Angle Dependence of Giant Magnetoresistance in Magnetic Superlattices

Giant magnetoresistance and structure of electrodeposited Co/Cu multilayers: the influence of layer thicknesses and Cu deposition potential

A Brief Introduction to Giant Magnetoresistance

Magnetoresistance Effect in Antiferromagnet/Nonmagnet/Antiferromagnet Multilayers

Large Low-Field Magnetoresistance Observed in Heterostructure Multilayers

Research Progress of Structure in Giant Magnetoresistance Multilayer Films

Simple Theory of Giant Magnetoresistance in a Magnetic Trilayer

A Method Of Separating The Giant Magnetoresistance And The Anisotropic Magnetoresistance In Multilayers

Inverse Giant Magnetoresistance in Magnetic Multilayers

Giant Magnetoresistance Properties in Granular Type (Co-Ag)/ag Multilayers