Dielectric, Multiferroic and Magnetodielectric Properties of (1-X)batio3-xsr(2)comoo(6) Solid Solution
Jingwei Li,Yongping Pu,Yu Shi,Ruike Shi,Xiaoying Wang,Mengdie Yang,Wen Wang,Xu Guo,Xin Peng
DOI: https://doi.org/10.1016/j.ceramint.2019.05.163
IF: 5.532
2019-01-01
Ceramics International
Abstract:The magnetoelectric composites of (1-x)BaTiO3-xSr(2)CoMoO(6) (x=0.02, 0.04, 0.06, 0.08, 0.10 and 0.12) are synthesized successfully via solid state reaction. The dielectric, multiferroic and magnetodielectric properties were discussed in details. The XRD data confirm the single perovskite phase among the composites. In addition, as the content of Sr2CoMoO6 increase, the diffraction peaks shift to higher angle which indicates the gradually decreased lattice parameters. The observed dielectric relaxation phenomenon could be attributed to MaxwellWagner (MW) model. The weak ferromagnetism was observed for x= 0.02, 0.04 with the remnant magnetization (M-r) 0.025 memu/g, 0.065 memu/g and coercivity (H-c) 4 Oe, 10 Oe, respectively despite the anti-ferromagnetic nature of Sr2CoMoO6. Furthermore, the M - H hysteresis loops of (1-x)BaTiO3-xSr(2)CoMoO(6) change obviously with polarization state, which is related to the ordering degree of the Co and Mo sites. The reason for observed magnetodielectric effect is the influence of magnetoresistance (MR) on Maxwell-Wagner (MW) effect.