Abstract:Sol-Gel-based reaction mixture sols have been long used to fabricate dense and uniform bioactive coatings with superior mechanical stability over metallic implants. On account of precise control over synthesis, fabrication, formed and low temperature of processing, this technology is one of the most feasible routes to produce bio-ceramic coatings. The study aims to develop a physical barrier over metal implants in form of bioinert Zirconia coatings, phase-stabilized using Dysprosium. The metallic substrates were cut into 10 mm × 10 mm samples and diamond polished after being polished with a 1000 grade emery sheet. Novel spin-coated zirconia films were fabricated over 316L Stainless steel substrates and were sintered at 600°C to obtain firm and uniform crack-free coatings. The thickness of the coatings was determined by ELCA-D meter thermal analysis was performed using TGA-DTA. Phase determination was performed using X-Ray diffraction followed by morphological investigations using Scanning electron microscopy. The corrosion resistance was evaluated with Polarization studies and electrokinetic data was derived using Tafel extrapolation. Biocompatibility evaluation was performed against MG-63 cell lines and RBCs along with bone-forming ability in vitro in SBF. Stable crack-free 3 Layer coatings fabricated at 2000 rpm for 3 s with a thickness of around 1 μm were found to be optimal for corrosion resistance behavior of steel implants at a low ICorr value of 0.501 µA/cm2 and adhesion strength of 40.93 MPa when untreated falling down to 39.92 MPa when immersed in SBF. The study concludes that medium rpm coatings sustain enough sol to produce crack-free coatings that form a strong physical barrier between body fluid and implant surface thereby reducing the attack of corrosive ions and protecting the implant surface without participating in any form of bioactivity but supporting native bone regeneration capabilities.

Macro-Residual Stress in 304 Stainless Steel Coated with Zro2-Ceo2 Thin Films by Sol-Gel Process

Study on the Macro-Residual Stress of 304 Stainless Steel Coated with Tio2-Sio2 Thin Films by Sol-Gel Process

Corrosion protection of stainless steel by ZrO2-CeO2 sol-gel coatings

Strain-induced Refinement and Thermal Stability of a Nanocrystalline Steel Produced by Surface Mechanical Attritiontreatment

Corrosion Protection of Stainless Steel by ZrO<sub>2</sub>-CeO<sub>2</sub> Sol-Gel Coatings

Corrosion and Tribological Behavior of ZrO2 Films Prepared on Stainless Steel Surface by the Sol-Gel Method

Preparation of Y2O3-Al2O3-ZrO2 Nano-Ceramic Coatings on Metal Substrate by Sol-Gel Method

Preparation of Y<sub>2</sub>O<sub>3</sub>-Al<sub>2</sub>O<sub>3</sub>-ZrO<sub>2</sub> Nano-Ceramic Coatings on Metal Substrate by Sol-Gel Method

XPS studies on composite ZrO2-CeO2 thin films deposited on metal substrate by sol-gel

Structural and electrochemical corrosion studies of spin coated ZrO2 thin films over stainless steel alloy for bone defect applications

Solidification microstructure and residual stress correlations in direct energy deposited type 316L stainless steel

Effects of Ultrasonic Nanocrystal Surface Modification on the Residual Stress, Microstructure, and Corrosion Resistance of 304 Stainless Steel Welds

Study of Interface Diffusion and Reaction Between Zr3N4 and Stainless Steel

Enhancing corrosion and mechanical properties of 304 stainless steel by depositing and annealing Zr75Cu25 thin-film metallic glass

The Growth Mechanism of the Colored Film on the Stainless Steel Studied by 18O Tracing and Nuclear Reaction Analysis

Effect of substrate temperature on microstructure and residual stress of EB-PVD ZrO2 coating

Development of Residual Stress in Sol-Gel Derived Pb(Zr,Ti)O-3 Films: an Experimental Study

Determination of residual stresses in Cu and Ag films on stainless steel substrates by cantilever beam method

Effect of Fast Multiple Rotation Rolling on the Oxidation Resistance of Super304H Stainless Steel in High-Temperature Water Vapor

The Effect of Zirconia Sol-Gel Coatings on Mild Steel Oxidation Resistance